MECHANISTIC STUDIES OF DIELECTRIC THIN-FILM GROWTH BY LOW-PRESSURE CHEMICAL VAPOR-DEPOSITION - THE REACTION OF TETRAETHOXYSILANE WITH SIO2 SURFACES

被引:77
作者
TEDDER, LL [1 ]
LU, GQ [1 ]
CROWELL, JE [1 ]
机构
[1] UNIV CALIF SAN DIEGO,DEPT CHEM,LA JOLLA,CA 92093
关键词
D O I
10.1063/1.348932
中图分类号
O59 [应用物理学];
学科分类号
摘要
The adsorption and reaction of tetraethoxysilane (TEOS) with hydroxylated SiO2 has been studied over the range of 100-450 K using transmission infrared spectroscopy. At 100 K, TEOS [Si(OC2H5)4] condenses on SiO2. Upon warming in vacuum, some of the condensed phase TEOS desorbs molecularly while a significant portion of the layer enters into a physisorption state. The physisorption state maximizes near 250 K, with strictly molecular desorption occurring upon warming to higher temperatures. When exposure occurs at 450 K, Si(OC2H5)4 reacts to form adsorbed siloxanes, thought to be a mixture of (SiO)2Si(OC2H5)2 and (SiO)Si(OC2H5)3. The adsorbed di- and triethoxysiloxanes decompose completely on heating in vacuum to 900 K. The chemistry of TEOS on SiO2 has been modeled using ethanol adsorption. Exposure of SiO2 to ethanol at 450 K leads to the formation of an adsorbed ethoxide species. Ethanol is shown to spectroscopically and chemically model the surface bound siloxanes produced upon reaction of Si(OC2H5)4 with hydroxylated SiO2 at 450 K. The vibrational spectrum of adsorbed ethoxide (SiOC2H5) is very similar to that of the adsorbed siloxanes produced from the adsorption of Si(OC2H5)4. The ethoxy modes are assigned through comparison of C2H5OH and CH3CD2OH adsorption. The temperature dependence of the decomposition of the adsorbed ethoxide is similar to that of the TEOS derived siloxanes. Decomposition of the adsorbed siloxanes is shown to evolve primarily ethylene.
引用
收藏
页码:7037 / 7049
页数:13
相关论文
共 37 条
[1]   RADIOLYSIS OF ETHANOL ADSORBED ON SILICA [J].
ABRAMS, L ;
ALLEN, AO .
JOURNAL OF PHYSICAL CHEMISTRY, 1969, 73 (08) :2741-&
[2]   DEPOSITION OF SILICON DIOXIDE FILMS AT REDUCED PRESSURE [J].
ADAMS, AC ;
CAPIO, CD .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1979, 126 (06) :1042-1046
[3]   LOW-PRESSURE DEPOSITION OF DOPED SIO2 BY PYROLYSIS OF TETRAETHYLORTHOSILICATE (TEOS) .1. BORON AND PHOSPHORUS DOPED FILMS [J].
BECKER, FS ;
ROHL, S .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1987, 134 (11) :2923-2931
[4]   PROCESS AND FILM CHARACTERIZATION OF LOW-PRESSURE TETRAETHYLORTHOSILICATE-BOROPHOSPHOSILICATE GLASS [J].
BECKER, FS ;
PAWLIK, D ;
SCHAFER, H ;
STAUDIGL, G .
JOURNAL OF VACUUM SCIENCE & TECHNOLOGY B, 1986, 4 (03) :732-744
[5]   LOW-PRESSURE DEPOSITION OF HIGH-QUALITY SIO2-FILMS BY PYROLYSIS OF TETRAETHYLORTHOSILICATE [J].
BECKER, FS ;
PAWLIK, D ;
ANZINGER, H ;
SPITZER, A .
JOURNAL OF VACUUM SCIENCE & TECHNOLOGY B, 1987, 5 (06) :1555-1563
[6]   INFRARED SPECTROSCOPIC OBSERVATIONS OF SURFACE BONDING IN PHYSICAL ADSORPTION - THE PHYSICAL ADSORPTION OF CO ON SIO2 SURFACES [J].
BEEBE, TP ;
GELIN, P ;
YATES, JT .
SURFACE SCIENCE, 1984, 148 (2-3) :526-550
[7]   INFRARED SPECTROSCOPIC STUDY OF THE ROTATION OF CHEMISORBED METHOXY SPECIES ON AN ALUMINA SURFACE [J].
BEEBE, TP ;
CROWELL, JE ;
YATES, JT .
JOURNAL OF CHEMICAL PHYSICS, 1990, 92 (08) :5119-5126
[8]   COMPETITIVE PHYSISORPTION - THE INTERACTION OF CO AND N-2 WITH SILICA SURFACES AS STUDIED BY IR SPECTROSCOPY [J].
BEEBE, TP ;
YATES, JT .
SURFACE SCIENCE, 1985, 159 (2-3) :369-380
[9]   HYDROGEN SPILLOVER ON ALUMINA - A STUDY BY INFRARED-SPECTROSCOPY [J].
CAVANAGH, RR ;
YATES, JT .
JOURNAL OF CATALYSIS, 1981, 68 (01) :22-26
[10]   INFRARED SPECTROSCOPIC OBSERVATIONS OF HYDROGEN-BONDING AND FERMI RESONANCE OF ADSORBED METHYL-CHLORIDE ON ALUMINA SURFACES [J].
CROWELL, JE ;
BEEBE, TP ;
YATES, JT .
JOURNAL OF CHEMICAL PHYSICS, 1987, 87 (06) :3668-3674