AUGER-ELECTRON INTENSITY VARIATIONS IN OXYGEN-CHARGED SILVER

Auger intensity variations over an oxygen-charged polycrystalline silver surface have been observed by studies of Auger images and line scans of selected adjacent grains which were determined to be the (421) and (221) orientations. The observed contrast (M4.5 VV transition) between the grains is produced by the variation in the detected Auger electrons caused by the different directions (interatomic direction) of forward focusing in each grain. The contrast produced by the Ag Auger electrons was found to be strongly dependent on the surface order of the grains, but that of the O Auger electrons was not, presumably becuase the atoms were dependent on the surface order of the grains, but that of the O Auger electrons was not, presumably because the atoms were randomly distributed throughout the Ag surface or subsurface. The contrast observed between the grains at the lower Auger energies (N1VV and N1N2.3V transitions) appeared to be produced by constructive interference from multiple scattering. The N1N2.3V electrons at 29 eV, for example, gave higher contrast than that of the N1VV transition at 78 eV.