Finite element analysis of stress distribution in thermal barrier coatings

被引:247
作者
Bialas, Marcin [1 ]
机构
[1] Inst Fundamental Technol Res, PL-00049 Warsaw, Poland
关键词
Creep; Burner rig test; Plasma spraying; Multilayer; Cohesive zone modelling;
D O I
10.1016/j.surfcoat.2008.06.178
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
A numerical simulation of crack development within APS TBC systems is presented. The TGO thickening and creep deformation of all system constituents is modelled. Two dimensional periodic unit cell is used to examine the effect of interfacial asperity on stress distribution and subsequent delamination of APS TBC. A study of cyclic loading and of creep of the base material on the stress distribution close to the asperity at the TGC/BC interface is made, revealing a small influence influence of both on the stress state in the thermal barrier coating system Subjected to temperature loading. Cohesive zone elements at the oxide/ceramic interface model the development of the interfacial micro-crack. The finite element analysis shows that the development of the interfacial crack allows for a micro-crack formation within APS TBC. Subsequent TGO growth results in a tensional zone within the oxide layer. Linking of the micro-cracks at the interface and within TBC through TGO Could lead to a coating delamination in the unit cell. (c) 2008 Elsevier B.V. All rights reserved
引用
收藏
页码:6002 / 6010
页数:9
相关论文
共 34 条
[31]   Cracking and decohesion of a thin Al2O3 film on a ductile Al-5%Mg substrate [J].
Xie, CJ ;
Tong, W .
ACTA MATERIALIA, 2005, 53 (02) :477-485
[32]   Stress and cracking behavior of plasma sprayed thermal barrier coatings using an advanced constitutive model [J].
Xie, WG ;
Jordan, E ;
Gell, M .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2006, 419 (1-2) :50-58
[33]   A numerical assessment of the durability of thermal barrier systems that fail by ratcheting of the thermally grown oxide [J].
Xu, T ;
He, MY ;
Evans, AG .
ACTA MATERIALIA, 2003, 51 (13) :3807-3820
[34]   Computational analysis of thin coating layer failure using a cohesive model and gradient plasticity [J].
Yuan, H ;
Chen, J .
ENGINEERING FRACTURE MECHANICS, 2003, 70 (14) :1929-1942