Fabrication of ordered macroporous rutile titania at low temperature

被引:16
作者
Kuang, DB [1 ]
Xu, AW [1 ]
Zhu, JY [1 ]
Liu, HQ [1 ]
Kang, BS [1 ]
机构
[1] Zhongshan Univ, Sch Chem & Chem Engn, Guangzhou 510275, Peoples R China
关键词
D O I
10.1039/b201245f
中图分类号
O6 [化学];
学科分类号
0703 ;
摘要
Macroporous rutile titania has been prepared by centrifugation sedimentation and evaporation approaches with TiCl4 as the precursor and polystyrene (PS) spheres as the template. The nanocrystalline rutile titania particles were first synthesized at room temperature, then used to fill the voids between the PS spheres. The macroporous material was obtained after calcination at 450degreesC. This is the first report of ordered macroporous rutile titania being obtained by calcination at such a low temperature. XRD results reveal that the titania nanoparticles of the as-synthesized and macroporous materials after calcination are rutile crystalline. SEM images show that the PS spheres and macroporous rutile form three-dimensionally ordered close-packed structures.
引用
收藏
页码:819 / 821
页数:3
相关论文
共 48 条
[41]  
2-J
[42]   INHIBITED SPONTANEOUS EMISSION IN SOLID-STATE PHYSICS AND ELECTRONICS [J].
YABLONOVITCH, E .
PHYSICAL REVIEW LETTERS, 1987, 58 (20) :2059-2062
[43]   PHOTONIC BAND-STRUCTURE - THE FACE-CENTERED-CUBIC CASE EMPLOYING NONSPHERICAL ATOMS [J].
YABLONOVITCH, E ;
GMITTER, TJ ;
LEUNG, KM .
PHYSICAL REVIEW LETTERS, 1991, 67 (17) :2295-2298
[44]   Development of one period of a three-dimensional photonic crystal in the 5-0 μm wavelength region by wafer fusion and laser beam diffraction pattern observation techniques [J].
Yamamoto, N ;
Noda, S ;
Chutinan, A .
JAPANESE JOURNAL OF APPLIED PHYSICS PART 2-LETTERS, 1998, 37 (9AB) :L1052-L1054
[45]  
Yan HW, 1999, ADV MATER, V11, P1003, DOI 10.1002/(SICI)1521-4095(199908)11:12<1003::AID-ADMA1003>3.0.CO
[46]  
2-K
[47]   Hierarchically ordered oxides [J].
Yang, PD ;
Deng, T ;
Zhao, DY ;
Feng, PY ;
Pine, D ;
Chmelka, BF ;
Whitesides, GM ;
Stucky, GD .
SCIENCE, 1998, 282 (5397) :2244-2246
[48]   A new route to three-dimensionally well-ordered macroporous rare-earth oxides [J].
Zhang, YG ;
Lei, ZB ;
Li, JM ;
Lu, SM .
NEW JOURNAL OF CHEMISTRY, 2001, 25 (09) :1118-1120