Surface degradation features and microstructural properties of ultra-high molecular weight polyethylene (UHMWPe)

Surface degradation of UHMWPe is recognized as a leading clinical concern, limiting the long-term performance in total knee replacements. Eight retrieved tibial plateaux and six wear screening test samples were evaluated for surface degradation features and microstructural features. The surface degradation features were assessed using stereomicroscopy and scanning electron microscopy. Microstructural features were evaluated using optical microscopy of thin cross-sections and a permanganate etching technique. The pitting mechanism of wear was observed on all eight retrieved TKR and covered an average of 12.6% of the surface area. The size of the pits were similar to the size of grains observed in the microstructural evaluation - approximately 100 to 200 mu m. The presented observations of pitting in retrieved knee implants have shown that the post-processing microstructure may influence this mechanism of surface degradation and hence the wear products.