Monitoring mechanical damage in structural materials using complimentary NDE techniques based on thermography and acoustic emission

被引：147

作者：

Kordatos, E. Z. ^{[1
]}

Aggelis, D. G. ^{[1
]}

Matikas, T. E. ^{[1
]}

机构：

[1] Univ Ioannina, Dept Mat Sci & Engn, GR-45110 Ioannina, Greece

来源：

COMPOSITES PART B-ENGINEERING | 2012年 / 43卷 / 06期

关键词：

Metal-matrix composites (MMCs); Fracture; IR thermography; Non-destructive testing; Acoustic emission; GROWTH; FRAGMENTATION; STEEL;

D O I：

10.1016/j.compositesb.2011.12.013

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

This work deals with nondestructive evaluation (NDE) of the fracture behavior of metallic materials by combining thermographic and acoustic emission (AE) characterization. A new procedure, based on lock-in infrared (IR) thermography, was developed to determine the crack growth rate using thermographic mapping of the material undergoing fatigue. The thermography results on crack growth rate were found to be in agreement with measurements obtained by the conventional compliance method. Furthermore. acoustic emission was used to record different cracking events. The rate of incoming signals, as well as qualitative features based on the waveform shape, was correlated with macroscopically measured mechanical parameters, such as load and crack propagation rate. Additionally, since the failure modes have distinct AE signatures, the dominant active fracture mode was identified in real time. The application of combined NDE techniques is discussed for characterizing the damage process which leads to catastrophic failure of the material, thereby enabling life prediction in both monolithic aluminum alloys and aluminum alloy/SiC particle (SiCp) reinforced composites. (C) 2012 Elsevier Ltd. All rights reserved.

引用

页码：2676 / 2686

页数：11

共 39 条

[21] Thermographic methodology for rapid determination of the fatigue limit of materials and mechanical components [J].

La Rosa, G ;

Risitano, A .

INTERNATIONAL JOURNAL OF FATIGUE, 2000, 22 (01) :65-73

[22] Fatigue limit evaluation of metals using an infrared thermographic technique [J].

Luong, MP .

MECHANICS OF MATERIALS, 1998, 28 (1-4) :155-163

[23] Experiments and analysis of fiber fragmentation in single and multiple-fiber SiC/Ti-6Al-4V metal matrix composites [J].

Majumdar, BS ;

Matikas, TE ;

Miracle, DB .

COMPOSITES PART B-ENGINEERING, 1998, 29 (02) :131-145

[24]

Maldague XPV, 2002, MATER EVAL, V60, P1060

[25] Microdeformationn behaviour of Al-SiC metal matrix composites [J].

Myriounis, D. P. ;

Hasan, S. T. ;

Matikas, T. E. .

COMPOSITE INTERFACES, 2008, 15 (05) :495-514

[26] Crack-Tip Stress Field and Fatigue Crack Growth Monitoring Using Infrared Lock-In Thermography in A359/SiCp Composites [J].

Myriounis, D. P. ;

Kordatos, E. Z. ;

Hasan, S. T. ;

Matikas, T. E. .

STRAIN, 2011, 47 :E619-E627

[27] Dissipated thermal energy and damage evolution of Glass/Epoxy using infrared thermography and acoustic emission [J].

Naderi, M. ;

Kahirdeh, A. ;

Khonsari, M. M. .

COMPOSITES PART B-ENGINEERING, 2012, 43 (03) :1613-1620

[28] Thermal NDI of resistance welded composite structures [J].

Nino, G. F. ;

Ahmed, T. J. ;

Bersee, H. E. N. ;

Beukers, A. .

COMPOSITES PART B-ENGINEERING, 2009, 40 (03) :237-248

[29]

Ohtsu M, 2008, ACI MATER J, V105, P194

[30] Recommendation of RILEM TC 212-ACD: acoustic emission and related NDE techniques for crack detection and damage evaluation in concrete Test method for classification of active cracks in concrete structures by acoustic emission [J].

Ohtsu, Masayasu ;

Shiotani, Tomoki ;

Shigeishi, M. ;

Kamada, T. ;

Yuyama, S. ;

Watanabe, T. ;

Suzuki, T. ;

van Mier, J. G. M. ;

Vogel, T. ;

Grosse, C. ;

Helmerich, R. ;

Forde, M. C. ;

Moczko, A. ;

Breysse, D. ;

Ivanovich, S. A. ;

Sajna, A. ;

Aggelis, D. ;

Lacidogna, G. .

MATERIALS AND STRUCTURES, 2010, 43 (09) :1187-1189

← 1 2 3 4 →