Preparation and magnetic properties of Nd5Fe95-xBx nanowire arrays

被引：18

作者：

Gao, Daqiang ^{[1
]}

Fu, Junli ^{[1
]}

Xu, Yan ^{[1
]}

Xue, Desheng ^{[1
]}

机构：

[1] Lanzhou Univ, Key Lab Magnetism & Magnet Mat MOE, Lanzhou 730000, Peoples R China

来源：

MATERIALS LETTERS | 2008年 / 62卷 / 17-18期

基金：

中国国家自然科学基金;

关键词：

magnetic properties; nanowire arrays; amorphous of Nd5Fe9-xBx;

D O I：

10.1016/j.matlet.2008.01.107

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Arrays of Nd5Fe95-xBx (17 <= x <= 28) nanowires were fabricated by electrodepositing in pores of anodic aluminum oxide (AAO) templates. Transmission electron microscope result shows that the nanowires are about 40 nm in diameter and the aspect ratio is approximately 75. Selected area electron diffraction and X-ray diffraction results indicate that the nanowires are amorphous in structure at concentration x=25. Vibrating sample magnetometer was employed to study the magnetic properties of nanowire arrays at room temperature. Due to the shape anisotropy effect, the arrays of nanowires exhibit obviously uniaxial magnetic anisotropy and the easy magnetizing axis is parallel to the nanowires. The coercivity with the magnetic field along the nanowire arrays decreases with the increasing of the B content. (c) 2008 Elsevier B.V. All rights reserved.

引用

页码：3070 / 3072

页数：3

共 23 条

[1]

BERRYA DC, 2007, J APPL PHYS, V102, P1

[2] Long-range atomic ordering and magnetic properties of Co1-xPtx/SiO2 granular films [J].

Chen, C ;

Kitakami, O ;

Okamoto, S ;

Shimada, Y .

JOURNAL OF APPLIED PHYSICS, 2000, 87 (09) :6947-6949

[3] Magnetic and structural properties of electrodeposited CoPt and FePt nanowires in nanoporous alumina templates [J].

Dahmane, Y. ;

Cagnon, L. ;

Voiron, J. ;

Pairis, S. ;

Bacia, M. ;

Ortega, L. ;

Benbrahim, N. ;

Kadri, A. .

JOURNAL OF PHYSICS D-APPLIED PHYSICS, 2006, 39 (21) :4523-4528

[4]

GHAI SS, 2004, J APPL PHYS, V97, P1

[5] Fabrication of carbon nanotube emitters in an anodic aluminium oxide nanotemplate on a Si wafer by multi-step anodization [J].

Hwang, SK ;

Lee, J ;

Jeong, SH ;

Lee, PS ;

Lee, KH .

NANOTECHNOLOGY, 2005, 16 (06) :850-858

[6] Growth and characterization of L10 FePt and CoPt ⟨001⟩ textured polycrystalline thin films [J].

Jeong, S ;

McHenry, ME ;

Laughlin, DE .

IEEE TRANSACTIONS ON MAGNETICS, 2001, 37 (04) :1309-1311

[7] Structure and magnetic properties of L10 CoPt(Ag/MgO,MgO) thin films [J].

Jeong, S ;

Hsu, YN ;

McHenry, ME ;

Laughlin, DE .

JOURNAL OF APPLIED PHYSICS, 2000, 87 (09) :6950-6952

[8] Nanocrystalline NdFeB magnets fabricated by a modified hot-working process [J].

Kim, H ;

Cho, S ;

Kim, Y ;

Kim, H ;

Kapustin, GA .

JOURNAL OF APPLIED PHYSICS, 2003, 93 (10) :8137-8139

[9] Additive blending effects on the magnetic properties of nanocrystalline NdFeB magnets [J].

Kim, HT ;

Kim, YB .

PHYSICA STATUS SOLIDI A-APPLICATIONS AND MATERIALS SCIENCE, 2004, 201 (08) :1938-1941

[10] Perpendicular magnetic anisotropy in sputtered amorphous TbFeCo films [J].

Liu, X. ;

Morisako, A. ;

Sakurai, H. ;

Sakurai, Y. ;

Itou, M. ;

Koizumi, A. .

JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 2007, 310 (02) :1744-1746

← 1 2 3 →