Formation and role of graphite and nickel silicide in nickel based ohmic contacts to n-type silicon carbide -: art. no. 083709

被引:125
作者
Nikitina, IP
Vassilevski, KV
Wright, NG
Horsfall, AB
O'Neill, AG
Johnson, CM
机构
[1] Newcastle Univ, Sch Elect Elect & Comp Engn, Newcastle Upon Tyne NE1 7RU, Tyne & Wear, England
[2] Univ Sheffield, Dept Elect & Elect Engn, Sheffield S1 3JD, S Yorkshire, England
基金
英国工程与自然科学研究理事会;
关键词
D O I
10.1063/1.1872200
中图分类号
O59 [应用物理学];
学科分类号
摘要
Nickel-based contacts, deposited on 4H-SiC C-face substrates, were annealed at temperatures ranging from 800 to 1040 degrees C and the phase composition of the contact layers analyzed by x-ray diffraction techniques. Ni2Si was identified as the dominant phase for annealing temperatures exceeding 925 degrees C, with further increases in concentration with increasing temperature. At the highest annealing temperature of 1040 degrees C, a 40 nm thick nanocrystalline graphite film at the Ni2Si-SiC interface was discovered and its presence confirmed by Raman spectroscopy. The roles of the Ni2Si and graphite films in the formation of ohmic contacts were determined by their subsequent exclusion from the contact composition. Following deposition and annealing, the Ni2Si and graphite layers were etched away selectively and replaced with new metal films deposited at room temperature and without any annealing. Measurement of the current-voltage characteristics revealed that the ohmic nature of the contacts was preserved after removal of the Ni2Si and the graphite layers. It is concluded that the main reason for the conversion of Schottky to ohmic contacts during high-temperature annealing is a change of the electrical properties of the underlying SiC rather than being attributable to the presence of nickel silicides or graphite. It is proposed that a solid-state reaction between nickel and silicon carbide, similar to catalytic graphitization of carbon, may take place during Ni-SiC contact annealing at the temperature of 1040 degrees C. This process may result in the creation of sufficient carbon vacancies in the near-interface region of the SiC to allow increased electron transport through the Schottky barrier. (C) 2005 American Institute of Physics.
引用
收藏
页数:7
相关论文
共 43 条
[1]  
Arnodo C, 1996, INST PHYS CONF SER, V142, P577
[2]   Ti/Ni/Ti/Au ohmic contact to n-type 6H-SiC [J].
Basak, D ;
Mahanty, S .
MATERIALS SCIENCE AND ENGINEERING B-SOLID STATE MATERIALS FOR ADVANCED TECHNOLOGY, 2003, 98 (02) :177-180
[3]  
Bozack MJ, 1997, PHYS STATUS SOLIDI B, V202, P549, DOI 10.1002/1521-3951(199707)202:1<549::AID-PSSB549>3.0.CO
[4]  
2-6
[5]   Positively charged carbon vacancy in 6H-SiC: EPR study [J].
Bratus, VY ;
Makeeva, IN ;
Okulov, SM ;
Petrenko, TL ;
Petrenko, TT ;
von Bardeleben, HJ .
PHYSICA B-CONDENSED MATTER, 2001, 308 :621-624
[6]   First- and second-order Raman scattering from semi-insulating 4H-SiC [J].
Burton, JC ;
Sun, L ;
Long, FH ;
Feng, ZC ;
Ferguson, IT .
PHYSICAL REVIEW B, 1999, 59 (11) :7282-7284
[7]  
Calcagno L, 2002, MATER SCI FORUM, V433-4, P721, DOI 10.4028/www.scientific.net/MSF.433-436.721
[8]   SiC microwave power technologies [J].
Clarke, RC ;
Palmour, JW .
PROCEEDINGS OF THE IEEE, 2002, 90 (06) :987-992
[9]   Fabrication and characterization of pulse laser deposited Ni2Si Ohmic contacts on n-SiC for high power and high temperature device applications [J].
Cole, MW ;
Joshi, PC ;
Ervin, M .
JOURNAL OF APPLIED PHYSICS, 2001, 89 (08) :4413-4416
[10]   SiC power-switching devices - The second electronics revolution? [J].
Cooper, JA ;
Agarwal, A .
PROCEEDINGS OF THE IEEE, 2002, 90 (06) :956-968