Oxidation characteristics of a platinized MCrAlY bond coat for TBC systems during cyclic oxidation at 1000 °C

被引：82

作者：

Quadakkers, WJ ^{[1
]}

Shemet, V ^{[1
]}

Sebold, D ^{[1
]}

Anton, R ^{[1
]}

Wessel, E ^{[1
]}

Singheiser, L ^{[1
]}

机构：

[1] Forschungszentrum Julich, D-52425 Julich, Germany

来源：

SURFACE & COATINGS TECHNOLOGY | 2005年 / 199卷 / 01期

关键词：

bond coat oxidation; MCrAlY; platinized; TBC;

D O I：

10.1016/j.surfcoat.2004.11.038

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

The scale growth mechanisms of a platinized NiCoCrAlY bond coat (BC) beneath a ceramic thermal barrier coating (TBC) were studied during cyclic oxidation in air at 1000 degrees C. The thermally grown oxide scales (TGO) after exposure times ranging from 100 to 9100 h were characterized by scanning electron microscopy and laser fluorescence spectroscopy. The TGO appeared to consist of alumina and no oxides of the other elements present in the NiCoCrAlY coating were detected. Up to exposure times of 1000 h substantial amounts of metastable alumina were found in the outer part of the TGO. This is probably the reason for the formation of a porous, mixed alumina/zirconia layer at the TBC/TGO interface. This layer was prone to micro-crack formation, which did, however, not result in macroscopic TBC failure. The latter occurred after crack formation at the TGO-BC interface. (c) 2004 Elsevier B.V. All rights reserved.

引用

页码：77 / 82

页数：6

共 24 条

[11] Some water vapor effects during the oxidation of alloys that are α-Al2O3 formers [J].

Maris-Sida, MC ;

Meier, GH ;

Pettit, FS .

METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2003, 34A (11) :2609-2619

[12]

MEIER SM, 1991, CR189111 NASA

[13] Influence of composition and phase distribution on the oxidation behaviour of NiCoCrAlY alloys [J].

Muñoz-Arroyo, R ;

Clemens, D ;

Tietz, F ;

Anton, R ;

Quadakkers, J ;

Singheiser, L .

HIGH TEMPERATURE CORROSION AND PROTECTION OF MATERIALS 5, PTS 1 AND 2, 2001, 369-3 :165-172

[14] As-deposited mixed zone in thermally grown oxide beneath a thermal barrier coating [J].

Murphy, KS ;

More, KL ;

Lance, MJ .

SURFACE & COATINGS TECHNOLOGY, 2001, 146 :152-161

[15] Effect of trace amounts of carbon and nitrogen on the high temperature oxidation resistance of high purity FeCrAl alloys [J].

Naumenko, D ;

Le-Coze, J ;

Wessel, E ;

Fischer, W ;

Quadakkers, WJ .

MATERIALS TRANSACTIONS, 2002, 43 (02) :168-172

[16] Pt and Hf additions to NiAl bond coats and their effect on the lifetime of thermal barrier coatings [J].

Nesbitt, JA ;

Gleeson, B ;

Sordelet, D ;

Barrett, CA .

THERMEC'2003, PTS 1-5, 2003, 426-4 :209-214

[17] Smart overlay coatings - concept and practice [J].

Nicholls, JR ;

Simms, NJ ;

Chan, W ;

Evans, HE .

SURFACE & COATINGS TECHNOLOGY, 2002, 149 (2-3) :236-244

[18]

Quadakkers WJ, 1999, ELEVATED TEMPERATURE COATINGS: SCIENCE AND TECHNOLOGY III, P119

[19] EFFECT OF THE THETA-ALPHA-AL2O3 TRANSFORMATION ON THE OXIDATION BEHAVIOR OF BETA-NIAL+ZR [J].

RYBICKI, GC ;

SMIALEK, JL .

OXIDATION OF METALS, 1989, 31 (3-4) :275-304

[20] Improved oxidation resistance of thermal barrier coatings [J].

Schmitt-Thomas, KG ;

Hertter, M .

SURFACE & COATINGS TECHNOLOGY, 1999, 120 :84-88

← 1 2 3 →