Assessment of the thermal stability of anodic alumina membranes at high temperatures

被引：46

作者：

Fernandez-Romero, L. ^{[1
]}

Montero-Moreno, J. M. ^{[2
]}

Pellicer, E. ^{[1
]}

Peiro, F. ^{[1
]}

Cornet, A. ^{[1
]}

Morante, J. R. ^{[1
]}

Sarret, M. ^{[2
]}

Muller, C. ^{[2
]}

机构：

[1] Univ Barcelona, Fac Fis, Dept Elect, EME CEMIC CeRMAE, E-08028 Barcelona, Spain

[2] Univ Barcelona, Fac Quim, Dept Quim Fis, Lab Electrodeposicio & Corrosio Electrodep, E-08028 Barcelona, Spain

来源：

MATERIALS CHEMISTRY AND PHYSICS | 2008年 / 111卷 / 2-3期

关键词：

aluminium oxide; AA1050; electrochemical techniques; annealing; X-ray diffraction;

D O I：

10.1016/j.matchemphys.2008.05.003

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The thermal stability of anodic alumina membranes (AAMs) annealed in air from 750 degrees C up to 1100 degrees C was investigated. AAMs were produced by single-step anodising of laminated AA1050 in 0.30M oxalic acid medium. The barrier layer provided thermal stability to the membranes, since it avoided or minimized bending and cracking phenomena. X-ray diffraction (XRD) analyses revealed that as-synthesized AAMs were amorphous and converted to polycrystalline after heat-treating above 750 degrees C. However, porous and barrier layers did not re-crystallize in the same way. The porous layer mainly crystallized in the gamma-Al2O3 phase within the range of 900-1100 degrees C, while the barrier layer was converted to the alpha-Al2O3 phase at 1100 degrees C. Different grain sizes were also estimated from Scherrer's formula. Scanning electron microscopy (SEM) images pointed out that cell wall dilation of the porous layer explained membrane cracking, which was avoided in presence of the barrier layer. (C) 2008 Elsevier B.V. All rights reserved.

引用

页码：542 / 547

页数：6

共 42 条

[1]

AKAHORI H, 1962, J ELECT MICROSCOPY J, V11, P217

[2] Direct formation of self-assembled nanoporous aluminium oxide on SiO2 and Si substrates [J].

Cai, AL ;

Zhang, HY ;

Hua, H ;

Zhang, ZB .

NANOTECHNOLOGY, 2002, 13 (05) :627-630

[3] Post-treatment method of producing ordered array of anodic aluminum oxide using general purity commercial (99.7%) aluminum [J].

Chen, CC ;

Chen, JH ;

Chao, CG .

JAPANESE JOURNAL OF APPLIED PHYSICS PART 1-REGULAR PAPERS BRIEF COMMUNICATIONS & REVIEW PAPERS, 2005, 44 (03) :1529-1533

[4] Self-ordered pore structure of anodized aluminum on silicon and pattern transfer [J].

Crouse, D ;

Lo, YH ;

Miller, AE ;

Crouse, M .

APPLIED PHYSICS LETTERS, 2000, 76 (01) :49-51

[5] Fabrication of controllable free-standing ultrathin porous alumina membranes [J].

Ding, GQ ;

Zheng, MJ ;

Xu, WL ;

Shen, WZ .

NANOTECHNOLOGY, 2005, 16 (08) :1285-1289

[6] Synthesis of semiconductor nanowires by pulsed current electrodeposition of metal with subsequent sulfurization [J].

Gavrilov, S ;

Nosova, L ;

Sieber, I ;

Belaidi, A ;

Dloczik, L ;

Dittrich, T .

PHYSICA STATUS SOLIDI A-APPLICATIONS AND MATERIALS SCIENCE, 2005, 202 (08) :1497-1501

[7] Nanostructuring titania by embossing with polymer molds made from anodic alumina templates [J].

Goh, C ;

Coakley, KM ;

McGehee, MD .

NANO LETTERS, 2005, 5 (08) :1545-1549

[8]

GOVYADINOV A, 2000, P ASME INT MECH ENG, V2, P313

[9]

Han CY, 2004, PLAT SURF FINISH, V91, P40

[10] Nanowires and 1D arrays fabrication:: An overview [J].

Hernández-Vélez, M .

THIN SOLID FILMS, 2006, 495 (1-2) :51-63

← 1 2 3 4 5 →