Comparative studies of perfluorinated lubricants adsorbed on hydrogenated amorphous carbon and amorphous carbon nitride

Temperature-programmed desorption and scanning force microscopy have been used to probe the interaction of a perfluorinated lubricant (Fomblin ZDOL) with hydrogenated amorphous carbon (a:C-H(x)) and amorphous carbon nitride (a:C-N(x)) substrates, two materials used as hard coatings in disk drive products. Temperature-programmed desorption measurements indicate that the nitride surfaces are more reactive toward this perfluorinated lubricant and, as a result, the thin lubricant film is more tightly bound to this substrate. Frictional force microscopy has been used to measure the coefficient of friction of the lubricated surfaces, 0.18 +/- 0.02 for both substrate materials, and finds that frictional properties of these interfaces in the low load regime are influenced more by the presence of the lubricant rather than the adsorbed state of the film. Likewise, similar disjoining pressures were measured for the lubricant adsorbed on the different coating materials and suggest that the ultrathin nature of the adsorbed lubricant film dominates this property rather than adsorption states.