New applications of nanocrystalline Fe(Co-Fe)-Hf-O magnetic films to micromagnetic devices

New applications of high resistivity magnetic films, such as Fe-Hf-O and Co-Fe-Hf-O as thin film inductors and flux gate magnetic sensors, were investigated. These soft magnetic films with nanocrystalline structure and high resistivity were deposited on glass substrate by using the oxygen reactive sputtering method. Planar sandwich thin film inductors developed by using Fe-Hf-O or Co-Fe-Hf-O films had a higher quality factor than that of an amorphous Co-Ta-Hf film inductor. The dc-dc converter using the Fe(Co-Fe)-Hf-O film inductor had higher conversion efficiency. These high resistivity magnetic films were also applied to a flux gate magnetic sensor operated at high frequencies over 1 MHz. Both high frequency excitation and high permeability (owing to the low eddy current loss) enabled us to increase the sensitivity, e.g., 39 mV/Oe/turn at 5 MHz when using a 3 mu m thick Fe-Hf-O film (12X6 mm(2) area). (C) 1998 American Institute of Physics.