Mechanisms for fatigue of micron-scale silicon structural films

被引:91
作者
Alsem, Daan Hein
Pierron, Olivier N.
Stach, Eric A.
Muhlstein, Christopher L.
Ritchie, Robert O.
机构
[1] Univ Calif Berkeley, Dept Mat Sci & Engn, Berkeley, CA 94720 USA
[2] Lawrence Berkeley Natl Lab, Div Sci Mat, Berkeley, CA 94720 USA
[3] Natl Ctr Electron Microscopy, Lawrence Berkeley Natl Lab, Berkeley, CA 94720 USA
[4] Qualcomm MEMS Technol Inc, San Jose, CA 95134 USA
关键词
D O I
10.1002/adem.200600269
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Although bulk silicon is not susceptible to fatigue, micron-scale silicon is. Several mechanisms have been proposed to explain this surprising behavior although the issue remains contentious. Here we review published fatigue results for micron-scale thin silicon films and find that in general they display similar trends, in that lower cyclic stresses result in larger number of cycles to failure in stress-lifetime data. We further show that one of two classes of mechanisms is invariably proposed to explain the phenomenon. The first class attributes fatigue to a surface effect caused by subcritical (stable) cracking in the silicon-oxide layer, e.g., reaction-layer fatigue; the second class proposes that subcritical cracking in the silicon itself is the cause of fatigue in Si films. It is our contention that results to date from single and polycrystalline silicon fatigue studies provide no convincing experimental evidence to support subcritical cracking in the silicon. Conversely, the reaction-layer mechanism is consistent with existing experimental results, and moreover provides a rational explanation for the marked difference between the fatigue behavior of bulk and micron-scale silicon.
引用
收藏
页码:15 / 30
页数:16
相关论文
共 67 条
[1]  
ALLAMEH S, 2001, MAT RES SOC S
[2]   Surface topography evolution and fatigue fracture in polysilicon MEMS structures [J].
Allameh, SM ;
Shrotriya, P ;
Butterwick, A ;
Brown, SB ;
Soboyejo, WO .
JOURNAL OF MICROELECTROMECHANICAL SYSTEMS, 2003, 12 (03) :313-324
[3]   Very high-cycle fatigue failure in micron-scale polycrystalline silicon films: Effects of environment and surface oxide thickness [J].
Alsem, D. H. ;
Timmerman, R. ;
Boyce, B. L. ;
Stach, E. A. ;
De Hosson, J. Th. M. ;
Ritchie, R. O. .
JOURNAL OF APPLIED PHYSICS, 2007, 101 (01)
[4]   Fatigue failure in thin-film polycrystalline silicon is due to subcritical cracking within the oxide layer [J].
Alsem, DH ;
Stach, EA ;
Muhlstein, CL ;
Ritchie, RO .
APPLIED PHYSICS LETTERS, 2005, 86 (04) :041914-1
[5]   Tensile-mode fatigue testing of silicon films as structural materials for MEMS [J].
Ando, T ;
Shikida, M ;
Sato, K .
SENSORS AND ACTUATORS A-PHYSICAL, 2001, 93 (01) :70-75
[6]   Fatigue of polycrystalline silicon under long-term cyclic loading [J].
Bagdahn, J ;
Sharpe, WN .
SENSORS AND ACTUATORS A-PHYSICAL, 2003, 103 (1-2) :9-15
[7]   THE FRACTURE OF SINGLE-CRYSTAL SILICON UNDER SEVERAL LIQUID ENVIRONMENTS [J].
CHEN, TJ ;
KNAPP, WJ .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1980, 63 (3-4) :225-226
[8]   MICROMECHANICAL FATIGUE TESTING [J].
CONNALLY, JA ;
BROWN, SB .
EXPERIMENTAL MECHANICS, 1993, 33 (02) :81-90
[9]   SLOW CRACK-GROWTH IN SINGLE-CRYSTAL SILICON [J].
CONNALLY, JA ;
BROWN, SB .
SCIENCE, 1992, 256 (5063) :1537-1539
[10]  
CONNALLY JA, 1991, INT C SOL STAT SENS