Hydrothermal epitaxy of KTaO3 thin films

Heteroepitaxial KTaO3 thin films were synthesized by the hydrothermal method below 175 degreesC in highly alkaline aqueous KOH solutions. KTaO3 films synthesized in 7 M KOH solutions contained a defect pyrochlore phase that had (400) and (111) out-of-plane orientations. The (400) oriented pyrochlore islands were epitaxially related to the (100) SrTiO3 substrate while the (I 11) oriented pyrochlore islands had four in-plane variants. Pyrochlore-free KTaO3 films could be synthesized in a 15 M KOH solution. Pyrochlore-free films were also grown at 7 M KOH by delaying the introduction of the (100) SrTiO3 substrate into the synthesis solution until the conditions favoring the formation of the pyrochlore phase had dissipated.