Subsolidus phase equilibria in the La2O3-CeO2-NiO system

被引:12
作者
Hrovat, M [1 ]
Holc, J [1 ]
Samardzija, Z [1 ]
Bernik, S [1 ]
机构
[1] Jozef Stefan Inst, Ljubljana 1000, Slovenia
关键词
D O I
10.1023/A:1006714909627
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The subsolidus phase equilibria at 1200 °C in air in the La2O3-CeO2-NiO system was investigated to elucidate the possible interactions between a ceria based electrolyte and lanthanum nickelate as a possible cathode material. No ternary compound was found. The tie lines were between the La2NiO4 and the end of CeO2 solid solution range with composition La0.5Ce0.5O1.75, and between the NiO and CeO2 range of solid solutions. Results indicated that lanthanum nickelate-based cathode material reacted with ceria-based solid electrolyte forming NiO and CeO2 solid solutions.
引用
收藏
页码:233 / 235
页数:3
相关论文
共 21 条
[1]  
BUCKREMER HP, 1997, P 5 INT S SOL OX FUE, P160
[2]  
COLOMER MT, 1998, P 3 EUR SOL OX FUEL, P55
[3]   AN ELECTRON-MICROSCOPE INVESTIGATION OF PHASES IN THE SYSTEM LA-NI-O [J].
DRENNAN, J ;
TAVARES, CP ;
STEELE, BCH .
MATERIALS RESEARCH BULLETIN, 1982, 17 (05) :621-626
[4]  
ECHIGOYA J, 1994, J MATER SCI LETT, V13, P1089
[5]  
GANULY P, 1973, MAT RES B, V8, P405
[6]   DEFECTS AND ELECTRICAL-CONDUCTION IN MIXED LANTHANUM TRANSITION-METAL OXIDES [J].
GAUR, K ;
VERMA, SC ;
LAL, HB .
JOURNAL OF MATERIALS SCIENCE, 1988, 23 (05) :1725-1728
[7]  
GODICKEMEIER M, 1997, J ELECTROCHEM SOC, V144, P1653
[8]  
GODICKEMEIER M, 1995, J ELECTROCHEM SOC, P1072
[9]   CRYSTALLOGRAPHIC, THERMAL AND ELECTROCHEMICAL PROPERTIES OF THE SYSTEM LA1-XSRXMNO3 FOR HIGH-TEMPERATURE SOLID ELECTROLYTE FUEL-CELLS [J].
HAMMOUCHE, A ;
SIEBERT, E ;
HAMMOU, A .
MATERIALS RESEARCH BULLETIN, 1989, 24 (03) :367-380
[10]   Subsolidus phase equilibria in the NiO-CeO2 and La2O3-CeO2-Fe2O3 systems [J].
Hrovat, M ;
Holc, J ;
Bernik, S ;
Makovec, D .
MATERIALS RESEARCH BULLETIN, 1998, 33 (08) :1175-1183