Novel coating systems produced by the combined cathodic arc/unbalanced magnetron sputtering for environmental protection of titanium alloys

被引：52

作者：

Leyens, C ^{[1
]}

Peters, M

Hovsepian, PE

Lewis, DB

Luo, Q

Münz, WD

机构：

[1] DLR German Aerosp Ctr, Mat Res Inst, D-51170 Cologne, Germany

[2] Sheffield Hallam Univ, Mat Res Inst, Sheffield S1 1WB, S Yorkshire, England

来源：

SURFACE & COATINGS TECHNOLOGY | 2002年 / 155卷 / 2-3期

关键词：

oxidation resistant coating; titanium alloys; combined cathodic arc/unbalanced magnetron sputtering; superlattice coating;

D O I：

10.1016/S0257-8972(02)00063-4

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

CrN/NbN, TiAlCrYN and TiAlYN/CrN coatings were deposited onto aerospace titanium alloy TIMETAL 834 using combined cathodic arc/unbalanced magnetron sputtering. Specimens were Nb- and Cr-ion etched before coating deposition, respectively. Isothermal and cyclic oxidation tests were performed in air at 750 degreesC for 1000 h. While CrN/NbN coatings as well as metal ion etching alone did not improve oxidation resistance of the substrate alloy, monolithically grown TiAlCrYN and superlattice TiAlYN/CrN coatings demonstrated enhanced oxidation resistance. TiAlCrYN provided improved oxidation resistance compared with commercial gamma-TiAl alloy Ti-48Al-2Cr-2Nb. Careful post-oxidation microstructural investigations using SEM, EDS, Raman spectroscopy. and TEM revealed that the TiAlCrYN and TiAlYN/CrN formed a thin protective alumina scale which was interrupted by titania agglomerations originating from substrate oxidation that dominated oxidation behaviour after extended exposure times. Despite the presence of coating defects leading to substrate attack, these novel coatings are considered as promising candidates for oxidation protection of titanium alloys. (C) 2002 Elsevier Science B.V All rights reserved.

引用

页码：103 / 111

页数：9

共 29 条

[1] Ion charge state distributions of vacuum arc plasmas: The origin of species [J].

Anders, A .

PHYSICAL REVIEW E, 1997, 55 (01) :969-981

[2] Titanium for aerospace: Rationale and applications [J].

Boyer, RR .

ADVANCED PERFORMANCE MATERIALS, 1995, 2 (04) :349-368

[3] The role of Cr in promoting protective alumina scale formation by gamma-based Ti-Al-Cr alloys .1. Compatibility with alumina and oxidation behavior in oxygen [J].

Brady, MP ;

Smialek, JL ;

Smith, J ;

Humphrey, DL .

ACTA MATERIALIA, 1997, 45 (06) :2357-2369

[4] The role of Cr in promoting protective alumina scale formation by gamma-based Ti-Al-Cr alloys .2. Oxidation behavior in air [J].

Brady, MP ;

Smialek, JL ;

Humphrey, DL ;

Smith, J .

ACTA MATERIALIA, 1997, 45 (06) :2371-2382

[5] Microstructure and oxidation-resistance of Til-x-y-zAlxCryYzN layers grown by combined steered-arc/unbalanced-magnetron-sputter deposition [J].

Donohue, LA ;

Smith, IJ ;

Munz, WD ;

Petrov, I ;

Greene, JE .

SURFACE & COATINGS TECHNOLOGY, 1997, 94-5 (1-3) :226-231

[6] MICROSTRUCTURES OF TIN FILMS GROWN BY VARIOUS PHYSICAL VAPOR-DEPOSITION TECHNIQUES [J].

HAKANSSON, G ;

HULTMAN, L ;

SUNDGREN, JE ;

GREENE, JE ;

MUNZ, WD .

SURFACE & COATINGS TECHNOLOGY, 1991, 48 (01) :51-67

[7] Recent progress in large scale manufacturing of multilayer/superlattice hard coatings [J].

Hovsepian, PE ;

Lewis, DB ;

Münz, WD .

SURFACE & COATINGS TECHNOLOGY, 2000, 133 :166-175

[8]

HOVSEPIAN PE, 1999, EUROMAT 99

[9] Joint second prize -: Significance of Y and Cr in TiAlN hard coatings for dry rich speed cutting [J].

Lembke, MI ;

Lewis, DB ;

Münz, WD ;

Titchmarsh, JM .

SURFACE ENGINEERING, 2001, 17 (02) :153-158

[10] The influence of the yttrium content on the structure and properties of Ti1-x-y-zAlxCryYzNPVD hard coatings [J].

Lewis, DB ;

Donohue, LA ;

Lembke, M ;

Münz, WD ;

Kuzel, R ;

Valvoda, V ;

Blomfield, CJ .

SURFACE & COATINGS TECHNOLOGY, 1999, 114 (2-3) :187-199

← 1 2 3 →