Hydrothermal doping of cobalt and magnetic properties in gamma iron oxide thin films

被引:3
作者
Chen, QW
Li, XG
Qian, YT
Zhang, YH
机构
[1] UNIV SCI & TECHNOL CHINA,ACAD SINICA,STRUCT RES LAB,BEIJING,PEOPLES R CHINA
[2] CTR ADV STUDIES SCI & TECHNOL MICROSTRUCT,NANJING 210093,PEOPLES R CHINA
[3] CCAST,WORLD LAB,BEIJING 100080,PEOPLES R CHINA
关键词
hydrothermal doping; cobalt; magnetic; gamma iron oxide; thin films;
D O I
10.1016/S0167-577X(96)00275-3
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
High coercivity (3.1 kOe) cobalt-doped gamma iron oxide (gamma-Fe2O3) thin films have been prepared by hydrothermal deposition of Fe3O4 followed by oxidation in air. Films deposited by hydrothermal treatment of a mixed solution of Fe(NO3)(3) . 9H(2)O and CoCl2 . 6H(2)O in the presence of reduced iron powder at 140 degrees C for 6 h have the Fe3O4 phase. Controlled oxidation in air at 400 degrees C for 2 h leads to the formation of gamma-Fe2O3 phase. The magnetic properties are enhanced, which is thought to be the result of well-crystallized acicular grains and uniform distribution of cobalt ions in the grains because of hydrothermal doping.
引用
收藏
页码:247 / 250
页数:4
相关论文
共 14 条
[1]   FERRITE PLATING IN AQUEOUS-SOLUTION - NEW TECHNIQUE FOR PREPARING MAGNETIC THIN-FILM [J].
ABE, M ;
TAMAURA, Y .
JOURNAL OF APPLIED PHYSICS, 1984, 55 (06) :2614-2616
[2]   EPITAXIAL-FILMS OF IRON-OXIDES GROWN BY THE METHOD OF CHEMICAL-TRANSPORT REACTION [J].
BABKIN, EV ;
KOVAL, KP ;
PYNKO, VG .
THIN SOLID FILMS, 1984, 117 (03) :217-221
[3]   LOW-TEMPERATURE SYNTHESIS OF BATIO3 THIN-FILMS ON SILICON SUBSTRATES BY HYDROTHERMAL REACTION [J].
BACSA, RR ;
DOUGHERTY, JP ;
PILIONE, LJ .
APPLIED PHYSICS LETTERS, 1993, 63 (08) :1053-1055
[4]   HYDROTHERMAL EPITAXY OF HIGHLY ORIENTED TIO2 THIN-FILMS ON SILICON [J].
CHEN, QW ;
QIAN, YT ;
CHEN, ZY ;
WU, WB ;
CHEN, ZW ;
ZHOU, GE ;
ZHANG, YH .
APPLIED PHYSICS LETTERS, 1995, 66 (13) :1608-1610
[5]   HYDROTHERMAL DEPOSITION OF MAGNETITE (FE3O4) THIN-FILMS [J].
CHEN, QW ;
QIAN, YT ;
CHEN, ZY ;
XIE, Y ;
ZHOU, GE ;
ZHANG, YH .
MATERIALS LETTERS, 1995, 24 (1-3) :85-87
[6]   DIRECT DEPOSITION OF HIGHLY COERCIVE GAMMA-IRON OXIDE THIN-FILMS FOR MAGNETIC RECORDING [J].
DHARA, S ;
RASTOGI, AC ;
DAS, BK .
JOURNAL OF APPLIED PHYSICS, 1993, 74 (11) :7019-7021
[7]   MAGNETIC RECORDING CHARACTERISTICS OF SPUTTERED GAMMA-FE2O3 THIN-FILM DISKS [J].
HATTORI, S ;
ISHII, Y ;
SHINOHARA, M ;
NAKAGAWA, T .
IEEE TRANSACTIONS ON MAGNETICS, 1979, 15 (06) :1549-1551
[8]  
HAYASHI M, 1990, J CERAM SOC JPN, V98, P930
[9]   CHARACTERISTICS OF COBALT ADSORBED IRON-OXIDE TAPES [J].
IMAOKA, Y ;
UMEKI, S ;
KUBOTA, Y ;
TOKUOKA, Y .
IEEE TRANSACTIONS ON MAGNETICS, 1978, 14 (05) :649-654
[10]   FERRITE THIN-FILMS FOR HIGH RECORDING DENSITY [J].
INAGAKI, N ;
HATTORI, S ;
ISHII, Y ;
TERADA, A ;
KATSURAKI, H .
IEEE TRANSACTIONS ON MAGNETICS, 1976, 12 (06) :785-787