Improved fatigue properties of lead zirconate titanate films made on oxygen-implanted platinum electrodes

被引：10

作者：

Chen, YC ^{[1
]}

Sun, YM ^{[1
]}

Gan, JY ^{[1
]}

机构：

[1] Natl Tsing Hua Univ, Dept Mat Sci & Engn, Hsinchu 30043, Taiwan

来源：

THIN SOLID FILMS | 2004年 / 460卷 / 1-2期

关键词：

X-ray photoelectron spectroscopy; grazing-incident X-ray diffractometer; ferroelectric properties; oxygen-implanted Pt electrode;

D O I：

10.1016/j.tsf.2004.01.056

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Pb(Zr0.3Ti0.7)O-3 (PZT) thin film capacitors fabricated on an oxygen-implanted Pt bottom electrode were studied. Oxygen was implanted at a low acceleration voltage (40 kV) and dose (1 x 10(15) cm(-2)). Structural examination by grazing-incident X-ray diffraction (GIXD) and chemical analysis by X-ray photoelectron spectroscopy (XPS) revealed that the implantation generated a very thin amorphous top surface layer (approx. 20 nm), which contained approximately 7% of oxygen that stayed in the film in the form of PtO bonding. The amorphous layer, however, resumed the crystalline structure accompanied by the dissociation of PtO under the rapid thermal annealing at 600 degreesC for 5 min. The remnant polarization of sol-gel derived Pb(Zr0.3Ti0.7)O-3 (PZT) films fabricated on the oxygen-implanted Pt was slightly reduced from 11.92 muC/cm(2) for the PZT capacitors fabricated on a Pt electrode without implanted oxygen to 9.07 muC/cm(2). Nevertheless, the fatigue endurance was significantly increased. The switching polarization of PtOx/PZT/Pt (O-implanted) capacitors remained within 95% of the starting value after 4 x 10(10) switching cycles, which is comparable to that of PZT capacitors made with other conducting oxides. (C) 2004 Elsevier B.V. All rights reserved.

引用

页码：25 / 29

页数：5

共 18 条

[11]

Moulder J. F., 1992, HDB XRAY PHOTOELECTR, P180

[12] PREPARATION OF PB(ZR,TI)O-3 THIN-FILMS ON ELECTRODES INCLUDING IRO2 [J].

NAKAMURA, T ;

NAKAO, Y ;

KAMISAWA, A ;

TAKASU, H .

APPLIED PHYSICS LETTERS, 1994, 65 (12) :1522-1524

[13] Effect of RuO2 growth temperature on ferroelectric properties of RuO2/Pb(Zr, Ti)O3/RuO2/Pt capacitors [J].

Norga, GJ ;

Fè, L ;

Wouters, DJ ;

Maes, HE .

APPLIED PHYSICS LETTERS, 2000, 76 (10) :1318-1320

[14] QUANTITATIVE MEASUREMENT OF SPACE-CHARGE EFFECTS IN LEAD ZIRCONATE-TITANATE MEMORIES [J].

SCOTT, JF ;

ARAUJO, CA ;

MELNICK, BM ;

MCMILLAN, LD ;

ZULEEG, R .

JOURNAL OF APPLIED PHYSICS, 1991, 70 (01) :382-388

[15] Activation field of ferroelectric (Pb,La)(Zr,Ti)O-3 thin film capacitors [J].

Song, TK ;

Aggarwal, S ;

Prakash, AS ;

Yang, B ;

Ramesh, R .

APPLIED PHYSICS LETTERS, 1997, 71 (15) :2211-2213

[16] Top-interface-controlled switching and fatigue endurance of (Pb, La)(Zr,Ti)O3 ferroelectric capacitors [J].

Stolichnov, I ;

Tagantsev, A ;

Setter, N ;

Cross, JS ;

Tsukada, M .

APPLIED PHYSICS LETTERS, 1999, 74 (23) :3552-3554

[17] PbZr0.5Ti0.5O3/La0.5Sr0.5CoO3 heterostructures prepared by chemical solution routes on silicon with no fatigue polarization [J].

Wang, GS ;

Meng, XJ ;

Sun, JL ;

Lai, ZQ ;

Yu, J ;

Guo, SL ;

Cheng, JG ;

Tang, J ;

Chu, JH .

APPLIED PHYSICS LETTERS, 2001, 79 (21) :3476-3478

[18] STUDY ON POLISHED AND ETCHED SURFACES OF POLAR (111) CDTE BY X-RAY PHOTOELECTRON-SPECTROSCOPY AND GRAZING-INCIDENCE X-RAY-DIFFRACTION [J].

WU, TB ;

CHEN, JS ;

CHIANG, CD ;

PANG, YM ;

YANG, SJ .

JOURNAL OF APPLIED PHYSICS, 1992, 71 (10) :5212-5216

← 1 2 →