Improved nitridation efficiency and mechanical property of stainless steel surface after N2-H2 plasma nitridation at low temperature

被引:17
作者
Marot, L [1 ]
Le Bourhis, E [1 ]
Straboni, A [1 ]
机构
[1] Univ Poitiers, SP2MI, CNRS,UMR 6630, Lab Met Phys Bd3, F-86960 Futuroscope, France
关键词
nitridation; plasma; steel; diffusion; nanoindentation; hardness; young modulus;
D O I
10.1016/S0167-577X(02)00421-4
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
In the thermochemical process of stainless steel nitridation, the improvement of mechanical properties is governed by the way the nitrogen diffusion profiles extend into the material. The efficiency of conventional thermal or ionic nitridation is substantially reduced at temperatures lower than 550 degreesC because of low nitrogen diffusivity. The present study shows that improved nitrogen transport can be obtained after nitridation in N-2-H-2 plasma at floating potential, that is without cathodic bias on the samples. Such cold conditions allow for the iron matrix to be nitrided in a depth range of 10 mum at a temperature as low as 430 degreesC. Under these conditions, the top surface hardness was increased by a factor of three. Using the nanoindentation technique on cross-sections prepared on plasma nitrided samples, we could determine the profiles of hardness and Young modulus. Unexpectedly, the Young modulus was shown to be almost unaffected by the treatment. Furthermore, hardness profiles correlated very well with the nitrogen chemical profile and the results showed that the interface between the treated layer and the untreated part of the sample was very abrupt. The high level of surface strengthening and the increased nitridation efficiency at low temperature are thought to be a consequence of an activation of surface transport and diffusion using plasma (cold) conditions at floating potential. (C) 2002 Elsevier Science B.V. All rights reserved.
引用
收藏
页码:76 / 79
页数:4
相关论文
共 9 条
[1]   The effect of hydrogen on the growth of the nitrided layer in r.f.-plasma-nitrided austenitic stainless steel AISI 316 [J].
Kumar, S ;
Baldwin, MJ ;
Fewell, MP ;
Haydon, SC ;
Short, KT ;
Collins, GA ;
Tendys, J .
SURFACE & COATINGS TECHNOLOGY, 2000, 123 (01) :29-35
[2]   Improved nitrogen transport in Fe-C alloys during NH3 plasma nitridation [J].
Marot, L ;
Pichon, L ;
Drouet, M ;
Straboni, A .
MATERIALS LETTERS, 2000, 44 (01) :35-38
[3]   AN IMPROVED TECHNIQUE FOR DETERMINING HARDNESS AND ELASTIC-MODULUS USING LOAD AND DISPLACEMENT SENSING INDENTATION EXPERIMENTS [J].
OLIVER, WC ;
PHARR, GM .
JOURNAL OF MATERIALS RESEARCH, 1992, 7 (06) :1564-1583
[4]   PHASE AND COMPOSITION DEPTH DISTRIBUTION ANALYSES OF LOW-ENERGY, HIGH-FLUX N-IMPLANTED STAINLESS-STEEL [J].
OZTURK, O ;
WILLIAMSON, DL .
JOURNAL OF APPLIED PHYSICS, 1995, 77 (08) :3839-3850
[5]   TRANSPORT NUMBER MEASUREMENTS DURING PLASMA ANODIZATION OF SI, GAAS, AND ZRSI2 [J].
PERRIERE, J ;
SIEJKA, J ;
REMILI, N ;
LAURENT, A ;
STRABONI, A ;
VUILLERMOZ, B .
JOURNAL OF APPLIED PHYSICS, 1986, 59 (08) :2752-2759
[6]   Nitrogen and oxygen transport and reactions during plasma nitridation of zirconium thin films [J].
Pichon, L ;
Straboni, A ;
Girardeau, T ;
Drouet, M ;
Widmayer, P .
JOURNAL OF APPLIED PHYSICS, 2000, 87 (02) :925-932
[7]  
SAKER A, 1991, MAT SCI ENG A-STRUCT, V87, P5326
[8]   SIGNIFICANCE OF NITROGEN MASS-TRANSFER MECHANISMS ON THE NITRIDING BEHAVIOR OF AUSTENITIC STAINLESS-STEEL [J].
SAMANDI, M ;
SHEDDEN, BA ;
BELL, T ;
COLLINS, GA ;
HUTCHINGS, R ;
TENDYS, J .
JOURNAL OF VACUUM SCIENCE & TECHNOLOGY B, 1994, 12 (02) :935-939
[9]   METASTABLE PHASE-FORMATION AND ENHANCED DIFFUSION IN FCC ALLOYS UNDER HIGH-DOSE, HIGH-FLUX NITROGEN IMPLANTATION AT HIGH AND LOW ION ENERGIES [J].
WILLIAMSON, DL ;
OZTURK, O ;
WEI, R ;
WILBUR, PJ .
SURFACE & COATINGS TECHNOLOGY, 1994, 65 (1-3) :15-23