Surface analysis of CVD carbon using NEXAFS, XPS and TEM

被引:23
作者
Kikuma, J [1 ]
Yoneyama, K
Nomura, M
Konishi, T
Hashimoto, T
Mitsumoto, R
Ohuchi, Y
Seki, K
机构
[1] Asahi Chem Ind Co Ltd, Analyt Res Lab, Fuji, Shizuoka 416, Japan
[2] Nagoya Univ, Fac Sci, Chikusa Ku, Nagoya, Aichi 46401, Japan
关键词
CVD carbon; NEXAFS; XPS; TEM; surface;
D O I
10.1016/S0368-2048(97)00220-X
中图分类号
O433 [光谱学];
学科分类号
0703 ; 070302 ;
摘要
Chemical and morphological characterization of carbon thin films produced by chemical vapor deposition (CVD) of hydrocarbon gases onto a hard carbon substrate has been performed using various surface analytical techniques. Semiquantitative analyses of the surface concentration of C=C double bonds have been conducted using near edge X-ray absorption fine structure (NEXAFS) at the C K edge and core level X-ray photoelectron spectroscopy (XPS). NEXAFS spectra of CVD carbon films are similar to those of well-ordered graphite. Rather surprisingly, however, it has been revealed that the CVD carbon films contain less C=C double bonds than that of the hard carbon. Intensities of pi-pi* shake-up satellite of the C Is XPS peak have been measured, and the results were consistent with those of NEXAFS. Smaller concentrations of C=C double bonds can be attributed to the incomplete dehydrogenation due to the relatively low temperature of the CVD treatment. High resolution transmission electron microscope (TEM) images of CVD carbon showed preferential orientation of graphite-like plane units in the direction parallel to the surface, suggesting the formation of large molecules in gas phase reaction prior to deposition. (C) 1998 Elsevier Science B.V.
引用
收藏
页码:919 / 925
页数:7
相关论文
共 15 条
  • [1] [Anonymous], CHEMISTRY PHYSICS CA
  • [2] CARBON-1S NEAR-EDGE-ABSORPTION FINE-STRUCTURE IN GRAPHITE
    BATSON, PE
    [J]. PHYSICAL REVIEW B, 1993, 48 (04): : 2608 - 2610
  • [3] COKE FORMATION DURING HYDROCARBONS PYROLYSIS .2. METHANE THERMAL-CRACKING
    BILLAUD, F
    BROUTIN, P
    BUSSON, C
    GUERET, C
    [J]. REVUE DE L INSTITUT FRANCAIS DU PETROLE, 1993, 48 (02): : 115 - 125
  • [4] CHARACTERIZATION OF TARS AND COKE FORMED DURING THE PYROLYSIS OF METHANE IN A TUBULAR REACTOR
    BLEKKAN, EA
    MYRSTAD, R
    OLSVIK, O
    ROKSTAD, OA
    [J]. CARBON, 1992, 30 (04) : 665 - 673
  • [5] PI-ASTERISK AND SIGMA-ASTERISK EXCITONS IN C-1S ABSORPTION OF GRAPHITE
    BRUHWILER, PA
    MAXWELL, AJ
    PUGLIA, C
    NILSSON, A
    ANDERSON, S
    MARTENSSON, N
    [J]. PHYSICAL REVIEW LETTERS, 1995, 74 (04) : 614 - 617
  • [6] TOTAL-ELECTRON-YIELD CURRENT MEASUREMENTS FOR NEAR-SURFACE EXTENDED X-RAY-ABSORPTION FINE-STRUCTURE
    ERBIL, A
    CARGILL, GS
    FRAHM, R
    BOEHME, RF
    [J]. PHYSICAL REVIEW B, 1988, 37 (05): : 2450 - 2464
  • [7] THERMAL COUPLING OF METHANE, EXPERIMENTAL INVESTIGATIONS ON COKE DEPOSITS
    GUERET, C
    BILLAUD, F
    FIXARI, B
    LEPERCHEC, P
    [J]. CARBON, 1995, 33 (02) : 159 - 170
  • [8] ISHITANI A, 1988, X SEN BUNSEKI NO SHI, V19, P127
  • [9] CHEMICAL VAPOR-DEPOSITION OF PYROLYTIC CARBON ON CARBON SUBSTRATES .1. EFFECT OF SUBSTRATE SURFACE CHARACTERISTICS ON THE KINETICS OF DEPOSITION
    ISMAIL, IMK
    ROSE, MM
    MAHOWALD, MA
    [J]. CARBON, 1991, 29 (4-5) : 575 - 585
  • [10] TEM INVESTIGATION OF CVD GRAPHITE ON NICKEL
    JOHANSSON, AS
    LU, J
    CARLSSON, JO
    [J]. THIN SOLID FILMS, 1994, 252 (01) : 19 - 25