Failure mechanism of Ta diffusion barrier between Cu and Si

被引:87
作者
Laurila, T
Zeng, KJ
Kivilahti, JK
Molarius, J
Suni, I
机构
[1] Helsinki Univ Technol, Lab Elect Prod Technol, FIN-02015 Espoo, Finland
[2] VTT Microelect, FIN-02044 Espoo, Finland
关键词
D O I
10.1063/1.1288692
中图分类号
O59 [应用物理学];
学科分类号
摘要
The reaction mechanisms in the Si/Ta/Cu metallization system and their relation to the microstructure of thin films are discussed on the basis of experimental results and the assessment of the ternary Si-Ta-Cu phase diagram at 700 degrees C. With the help of sheet resistance measurements, Rutherford backscattering spectroscopy, x-ray diffraction, a scanning electron microscope, and a transmission electron microscope, the Ta barrier layer was observed to fail at temperatures above 650 degrees C due to the formation of TaSi2, the diffusion of Cu through the silicide layer, and the resulting formation of Cu3Si precipitates. However, in order for the TaSi2 phase to form first, the Ta diffusion barrier layer must be thick enough (e.g., 50-100 nm) to prevent Cu diffusion into the Si substrate up to the temperature of TaSi2 formation (similar to 650 degrees C). Independent of the Ta layer thickness, Cu3Si was present as large nodules, whereas the TaSi2 existed as a uniform layer. The resulting reaction structure was found to be in local equilibrium on the basis of the assessed Si-Ta-Cu phase diagram at 700 degrees C, and therefore no further reactions were expected. The role of oxygen was also found to be important in the reactions and it seems to have a strong effect on the thermal stability of the barrier layer. (C) 2000 American Institute of Physics. [S0021-8979(00)06318-0].
引用
收藏
页码:3377 / 3384
页数:8
相关论文
共 37 条
[31]   Study of nanocrystalline Ta(N,O) diffusion barriers for use in Cu metallization [J].
Stavrev, M ;
Fischer, D ;
Preuss, A ;
Wenzel, C ;
Mattern, N .
MICROELECTRONIC ENGINEERING, 1997, 33 (1-4) :269-275
[32]   THE FORMATION OF CU3SI - MARKER EXPERIMENTS [J].
STOLT, L ;
DHEURLE, FM .
THIN SOLID FILMS, 1990, 189 (02) :269-274
[33]   ADVANCED COPPER INTERCONNECTIONS FOR SILICON CMOS TECHNOLOGIES [J].
TORRES, J .
APPLIED SURFACE SCIENCE, 1995, 91 (1-4) :112-123
[34]  
TU KN, 1978, THIN FILM INTERDIFFU, P360
[35]   A THERMODYNAMIC EVALUATION OF 4 SI-MO, SI-TA, SI-TI, SI-W BINARY-SYSTEMS [J].
VAHLAS, C ;
CHEVALIER, PY ;
BLANQUET, E .
CALPHAD-COMPUTER COUPLING OF PHASE DIAGRAMS AND THERMOCHEMISTRY, 1989, 13 (03) :273-292
[36]   TRANSITION-METALS IN SILICON [J].
WEBER, ER .
APPLIED PHYSICS A-MATERIALS SCIENCE & PROCESSING, 1983, 30 (01) :1-22
[37]   Tantalum-microcrystalline CeO2 diffusion barrier for copper metallization [J].
Yoon, DS ;
Baik, HK ;
Lee, SM .
JOURNAL OF APPLIED PHYSICS, 1998, 83 (03) :1333-1336