Materials challenges for CdTe and CuInSe2 photovoltaics

被引:40
作者
Beach, Joseph D.
McCandless, Brian E.
机构
关键词
D O I
10.1557/mrs2007.26
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The record laboratory cell (similar to 1 cm(2) area) efficiency for thin-film cadmium telluride (CdTe) is 16.5%, and that for a copper indium diselenide (CulnSe(2)) thin-film alloy is 19.5%. Commercially produced CdTe and CulnSe(2) modules (0.5-1 m(2) area) have efficiencies in the 7-11% range. Research is needed both to increase laboratory cell efficiencies and to bring those small-area efficiencies to large-area production. Increases in laboratory CdTe cell efficiency will require increasing open-circuit voltage, which will allow cells to harvest more energy from each absorbed photon. This will require extending the minority carrier lifetime from its present tau <= 2 ns to tau <= 10 ns and increasing hole concentration in the CdTe beyond 10(15) cm(2), which appears to be limited by compensating defects. Increasing laboratory CuInSe2-based cell efficiency significantly beyond 19.5% will also require increasing the open-circuit voltage, either by increasing the bandgap, the doping level, or the minority carrier lifetime. The photovoltaic cells in commercial modules occupy tens of square centimeters, and both models and experiments have shown that low-performing regions in small fractions of a cell can significantly reduce the overall cell performance. Increases in commercial module efficiency will require control of materials properties across large deposition areas in a high-throughput environment to minimize such non-uniformities. This article discusses approaches used and research needed to increase the ultimate efficiencies of CdTe- and CulnSe(2)-based devices and translate these gains to commercial photovoltaic modules.
引用
收藏
页码:225 / 229
页数:5
相关论文
共 20 条
  • [11] Mickelsen R. A., 1981, Fifteenth IEEE Photovoltaic Specialists Conference - 1981, P800
  • [12] Effects of CdCl2 treatment on the recrystallization and electro-optical properties of CdTe thin films
    Moutinho, HR
    Al-Jassim, MM
    Levi, DH
    Dippo, PC
    Kazmerski, LL
    [J]. JOURNAL OF VACUUM SCIENCE & TECHNOLOGY A-VACUUM SURFACES AND FILMS, 1998, 16 (03): : 1251 - 1257
  • [13] THE SPECTRAL P-N-JUNCTION MODEL FOR TANDEM SOLAR-CELL DESIGN
    NELL, ME
    BARNETT, AM
    [J]. IEEE TRANSACTIONS ON ELECTRON DEVICES, 1987, 34 (02) : 257 - 266
  • [14] n-type doping of CuInSe2 and CuGaSe2 -: art. no. 035211
    Persson, C
    Zhao, YJ
    Lany, S
    Zunger, A
    [J]. PHYSICAL REVIEW B, 2005, 72 (03)
  • [15] Polycrystalline heterojunction solar cells: A device perspective
    Phillips, JE
    Birkmire, RW
    McCandless, BE
    Meyers, PV
    Shafarman, WN
    [J]. PHYSICA STATUS SOLIDI B-BASIC SOLID STATE PHYSICS, 1996, 194 (01): : 31 - 39
  • [16] Development of thin-film Cu(In,Ga)Se2 and CdTe solar cells
    Romeo, A
    Terheggen, A
    Abou-Ras, D
    Bätzner, DL
    Haug, FJ
    Kälin, M
    Rudmann, D
    Tiwari, AN
    [J]. PROGRESS IN PHOTOVOLTAICS, 2004, 12 (2-3): : 93 - 111
  • [17] Chemical and structural characterization of Cu(In,Ga)Se-2/Mo interface in Cu(In,Ga)Se-2 solar cells
    Wada, T
    Kohara, N
    Negami, T
    Nishitani, M
    [J]. JAPANESE JOURNAL OF APPLIED PHYSICS PART 2-LETTERS & EXPRESS LETTERS, 1996, 35 (10A): : L1253 - L1256
  • [18] Manufacturable large area CdS thin films for solar cell applications monitored with optical emission spectroscopy
    Wang, L
    Eisgruber, I
    Hollingsworth, R
    DeHart, C
    Wangensteen, T
    Treece, RE
    Bhat, P
    Shafarman, WN
    Birkmire, RW
    Gillespie, TJ
    [J]. IN SITU PROCESS DIAGNOSTICS AND MODELLING, 1999, 569 : 127 - 132
  • [19] Chemical trends of defect formation and doping limit in II-VI semiconductors: The case of CdTe
    Wei, SH
    Zhang, SB
    [J]. PHYSICAL REVIEW B, 2002, 66 (15) : 1 - 10
  • [20] High-efficiency polycrystalline CdTe thin-film solar cells
    Wu, XZ
    [J]. SOLAR ENERGY, 2004, 77 (06) : 803 - 814