PREPARATION AND PROPERTIES OF SI-CONTAINING COPOLYMER FOR NEAR-UV RESIST .1. POLY(N-(4-HYDROXYPHENYL)MALEIMIDE-ALT-PARA-TRIMETHYLSILYLSTYRENE)

被引:20
作者
CHIANG, WY
LU, JY
机构
[1] Department of Chemical Engineering, Tatung Institute of Technology, Taipei, 10415, 40 Chungshan North Road
关键词
D O I
10.1002/pola.1991.080290313
中图分类号
O63 [高分子化学(高聚物)];
学科分类号
070305 ; 080501 ; 081704 ;
摘要
A new negative near-UV photoresist consisting of poly(N-(4-hydroxyphenyl) maleimidealt-p-trimethylsilylstyrene) (PHMS) and a naphthoquinonediazide ester was developed. PHMS was synthesized by solution free-radical polymerization of the comonomers with azobisisobutyronitrile (AIBN) in 1,4-dioxane at 60-degrees-C. The preparation of PHMS in terms of reaction time, thermal initiator, and solvent was evaluated; and a series of different molecular weight copolymers were prepared. PHMS was 1 : 1 in composition and was predominantly alternating. These copolymers dissolved in a wide range of solvents (including 5% tetramethylammonium hydroxide). The thermal properties of these copolymers were investigated by DSC and TGA. The chain-stiffening effect of the maleimide group played an important role in effecting high thermal resistance. Near-UV exposure was carried out using a Canon PLA-501F contact printer. High resolution negative images were obtained which had resistance to thermal deformation at 330-degrees-C and above. The developed patterns exhibited good adhesion to the silicon substrates without the use of an adhesion promoter. The lithographic applications of a bilayer photoresist system in which the prepared resist was used as the top imaging layer were examined. It is supposed that if PHMS was used as a binder for a diazonaphthoquinone sulfonate (NDS) photochemically, positive images would be obtained; however, on the contrary, negative images were observed. It is proposed that photocrosslinking occurred in the PHMS main chain.
引用
收藏
页码:399 / 410
页数:12
相关论文
共 28 条
[1]   FREE-RADICAL COPOLYMERIZATIONS OF N-PHENYL MALEIMIDE [J].
BARRALESRIENDA, JM ;
GONZALEZDELACAMPA, JI ;
RAMOS, JG .
JOURNAL OF MACROMOLECULAR SCIENCE-CHEMISTRY, 1977, A 11 (02) :267-286
[2]  
CERNIGLIARO GJ, 1984, Patent No. 4439516
[3]  
COTTON FA, 1988, ADV INORG CHEM RAD, P290
[4]   THE GLASS TEMPERATURE AND RELATED PROPERTIES OF POLYSTYRENE - INFLUENCE OF MOLECULAR WEIGHT [J].
FOX, TG ;
FLORY, PJ .
JOURNAL OF POLYMER SCIENCE, 1954, 14 (75) :315-319
[5]  
Gordon A. J., 1972, CHEM COMPANION, P113
[6]   POLY(ALKENYLSILANE SULFONE)S AS POSITIVE ELECTRON-BEAM RESISTS FOR 2-LAYER SYSTEMS [J].
GOZDZ, AS ;
CRAIGHEAD, HG ;
BOWDEN, MJ .
POLYMER ENGINEERING AND SCIENCE, 1986, 26 (16) :1123-1128
[7]   DEEP UV PHOTORESIST CONTAINING ORTHO-NITROBENZYLSILYLETHER STRUCTURE IN THE MAIN CHAIN [J].
HAYASE, S ;
ONISHI, Y ;
HORIGUCHI, R .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1987, 134 (09) :2275-2280
[8]   SYNTHESIS OF "POLY(P-HYDROXY-ALPHA-METHYLSTYRENE) BY CATIONIC POLYMERIZATION AND CHEMICAL MODIFICATION [J].
ITO, H ;
WILLSON, CG ;
FRECHET, JMJ ;
FARRALL, MJ ;
EICHLER, E .
MACROMOLECULES, 1983, 16 (04) :510-517
[9]  
IWASAKI M, 1979, Patent No. 4139384
[10]  
LIN BJ, 1983, ACS SYM SER, V219, P187