EROSION-RESISTANT AND CORROSION-RESISTANT COATINGS FOR AIRCRAFT COMPRESSOR BLADES

被引：36

作者：

SWADZBA, L

FORMANEK, B

GABRIEL, HM

LIBERSKI, P

PODOLSKI, P

机构：

[1] Silesian Technical University, 40-018 Katowice

来源：

SURFACE & COATINGS TECHNOLOGY | 1993年 / 62卷 / 1-3期

关键词：

D O I：

10.1016/0257-8972(93)90288-Y

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

In this paper the comparative test results of protective properties of several coatings for aircraft engine compressor blades are presented. Erosion and corrosion tests for the base metals and coatings were carried out. Corrosion test for base materials and anodic coating was made in neutral salt spray. For cathodic coatings a modified corrosion test was performed. It has been determined that the coatings obtained by physical vapour deposition (PVD), particularly (Ti, Al)N and TiN(Pt) are the best in the erosion and corrosion test conditions. The electroplated Ni-Cd coatings do not show satisfactory erosion resistance, but they have good corrosion resistance. It seems that PVD coatings fulfil the requirements for the protection of aero engine compressor blades.

引用

页码：486 / 492

页数：7

共 17 条

[1]

BORBECK KD, 1993, DVS BER, V152, P57

[2]

BORBECK KD, 1993, MAR P THERM SPRAYING

[3] A STUDY OF THE CORROSION BEHAVIOR OF TIN FILMS [J].

ERDEMIR, A ;

CARTER, WB ;

HOCHMAN, RF ;

MELETIS, EI .

MATERIALS SCIENCE AND ENGINEERING, 1985, 69 (01) :89-93

[4]

Flanagan J. E., 1976, U. S. Patent, Patent No. [3,948,697, 3948697]

[5]

JEHN HA, 1992, 19TH P INT C MET COA, V1, P108

[6]

LOWDEN P, 1990, CAN AERONAUT SPACE J, V36, P25

[7]

NAGY D, 1991, ADV AEROSPACE MATERI

[8] TITANIUM NITRIDE COATING FOR AERO ENGINE COMPRESSOR GAS PATH COMPONENTS [J].

PARAMESWARAN, VR ;

IMMARIGEON, JP ;

NAGY, D .

SURFACE & COATINGS TECHNOLOGY, 1992, 52 (03) :251-260

[9] CORROSION PERFORMANCE OF LAYERED COATINGS PRODUCED BY PHYSICAL VAPOR-DEPOSITION [J].

PARK, MJ ;

LEYLAND, A ;

MATTHEWS, A .

SURFACE & COATINGS TECHNOLOGY, 1990, 43-4 (1-3) :481-492

[10]

PARKER DW, 1991, ADV MATER PROCESS, V139, P68

← 1 2 →