SIO2 PRECIPITATE STRAIN RELIEF IN CZOCHRALSKI SI - SELF-INTERSTITIAL EMISSION VERSUS PRISMATIC DISLOCATION LOOP PUNCHING

被引:29
作者
TAYLOR, WJ [1 ]
GOSELE, U [1 ]
TAN, TY [1 ]
机构
[1] MICROELECTR CTR N CAROLINA,RES TRIANGLE PK,NC 27709
关键词
D O I
10.1063/1.351610
中图分类号
O59 [应用物理学];
学科分类号
摘要
Formation of SiO2 precipitates in Czochralski Si is associated with a volume expansion of more than 100%. The needed extra volume for precipitate growth to occur is primarily supplied by emission of Si self-interstitials (I) into the Si matrix, in balance with a compressive growth residual strain. During cooling after the anneal, an additional compressive cooling strain component also develops because of the different thermal expansion coefficients of SiO2 and Si. For precipitates grown to a sufficiently large size, the growth residual strain and/or the cooling strain can be further relieved by punching interstitial type prismatic dislocation loops into the Si matrix. Otherwise, only I emission can occur. Up to now, there have been no quantitatively determined strain values, which constitute in a given experiment a measure of the I emission efficiency on the one hand, and a basis for determining whether prismatic punching can also occur on the other. In this study, we have calculated the strain values and obtained a quantitative criterion for prismatic punching to occur. In the order of approximately 10(-3)-10(-2), the growth residual strain component values indicate that I emission has attained an efficiency of relieving the precipitate growth strain by approximately 90%-99%. Available experimental data on the precipitate size dependence of prismatic dislocation loop punching have been satisfactorily fitted using the obtained strain values and the punching criterion, indicating that these calculated values are in acceptable accuracy ranges.
引用
收藏
页码:2192 / 2196
页数:5
相关论文
共 20 条
[1]   ON GENERATION OF DISLOCATIONS AT MISFITTING PARTICLES IN A DUCTILE MATRIX [J].
ASHBY, MF ;
JOHNSON, L .
PHILOSOPHICAL MAGAZINE, 1969, 20 (167) :1009-&
[2]   CONFIGURATION + DIFFUSION OF ISOLATED OXYGEN IN SILICON + GERMANIUM [J].
CORBETT, JW ;
MCDONALD, RS ;
WATKINS, GD .
JOURNAL OF PHYSICS AND CHEMISTRY OF SOLIDS, 1964, 25 (08) :873-&
[3]  
CRAVEN RA, 1981, SEMICONDUCTOR SILICO, P254
[4]   DETERMINATION OF PARTS PER BILLION OXYGEN IN SILICON THROUGH CALIBRATION OF IR-ABSORPTION AT 77 DEGREES KELVIN [J].
GRAFF, K ;
GRALLATH, E ;
ADES, S ;
GOLDBACH, G ;
TOLG, G .
SOLID-STATE ELECTRONICS, 1973, 16 (08) :887-893
[5]  
HASEBE M, 1992, MATER SCI FORUM, V83, P1475, DOI 10.4028/www.scientific.net/MSF.83-87.1475
[6]  
HU SM, 1986, MATER RES SOC S P, V59, P249
[7]  
INOUE N, 1981, SEMICONDUCTOR SILICO, P282
[8]  
LAWRENCE JD, 1986, MATER RES SOC S P, V59, P389
[9]   CHARACTERIZATION OF STRUCTURAL DEFECTS IN ANNEALED SILICON CONTAINING OXYGEN [J].
MAHER, DM ;
STAUDINGER, A ;
PATEL, JR .
JOURNAL OF APPLIED PHYSICS, 1976, 47 (09) :3813-3825
[10]  
PONCE FA, 1984, ELECTRON MICROS, V31, P153