CRACKING AND DELAMINATION OF METAL-ORGANIC VAPOR-DEPOSITED ALUMINA AND SILICA FILMS

被引：18

作者：

HAANAPPEL, VAC ^{[1
]}

VANCORBACH, HD ^{[1
]}

FRANSEN, T ^{[1
]}

GELLINGS, PJ ^{[1
]}

机构：

[1] UNIV TWENTE,DEPT CHEM TECHNOL,POB 217,ENSCHEDE,NETHERLANDS

来源：

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 1993年 / 167卷 / 1-2期

关键词：

D O I：

10.1016/0921-5093(93)90352-F

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

Amorphous alumina and silica films were deposited on AISI 304 by thermal decomposition at atmospheric pressure of aluminium-tri-sec-butoxide and di-acetoxy-di-tertiary-butoxide-silane respectively. Above a critical coating thickness of the oxide films, cracking and delamination occurred during the deposition process. These were due to intrinsic rather than to thermal stresses. Cracking and delamination do not occur simultaneously. The fracture toughness of the film, the substrate and the interface is an important factor. After delamination along the substrate-film interface, the films curled to scrolls, indicating stress. A complete explanation of the stress gradient formed in the film during the deposition process is not yet available.

引用

页码：179 / 185

页数：7

共 21 条

[1] RESIDUAL-STRESS CRACKING OF METAL CERAMIC BONDS
BARTLETT, A
EVANS, AG
RUHLE, M
[J]. ACTA METALLURGICA ET MATERIALIA, 1991, 39 (07): : 1579 - 1585
[2] FUNDAMENTALS OF CHEMICAL VAPOR-DEPOSITION
BRYANT, WA
[J]. JOURNAL OF MATERIALS SCIENCE, 1977, 12 (07) : 1285 - 1306
[3] THE STRENGTH OF CERAMICS BONDED WITH METALS
DALGLEISH, BJ
LU, MC
EVANS, AG
[J]. ACTA METALLURGICA, 1988, 36 (08): : 2029 - 2035
[4] STRESS AND STRUCTURAL RELAXATION IN METALLOORGANIC CHEMICAL VAPOR-DEPOSITED SIO2-FILMS
DESU, SB
[J]. JAPANESE JOURNAL OF APPLIED PHYSICS PART 2-LETTERS & EXPRESS LETTERS, 1991, 30 (12B): : L2123 - L2126
[5] DESU SB, 1989, MATER RES SOC S P, V168, P221
[6] EXPERIMENTAL-OBSERVATIONS OF SUBSTRATE FRACTURE CAUSED BY RESIDUALLY STRESSED FILMS
DRORY, MD
EVANS, AG
[J]. JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1990, 73 (03) : 634 - 638
[7] ON THE MECHANICAL-BEHAVIOR OF BRITTLE COATINGS AND LAYERS
EVANS, AG
CRUMLEY, GB
DEMARAY, RE
[J]. OXIDATION OF METALS, 1983, 20 (5-6): : 193 - 216
[8] FISHER RM, 1990, MATER RES SOC SYMP P, V188, P257, DOI 10.1557/PROC-188-257
[9] HAANAPPEL VAC, IN PRESS P C HIGH TE
[10] Hu M.-S., 1988, MATER RES SOC S P, V130, DOI [10.1557/proc-130-213., DOI 10.1557/PROC-130-213]

← 1 2 3 →