SELECTIVE CHEMICAL-VAPOR-DEPOSITION OF COPPER USING (HFAC) COPPER(I) VINYLTRIMETHYLSILANE IN THE ABSENCE AND PRESENCE OF WATER

被引:39
作者
JAIN, A
GELATOS, AV
KODAS, TT
HAMPDENSMITH, MJ
MARSH, R
MOGAB, CJ
机构
[1] UNIV NEW MEXICO,DEPT CHEM,ALBUQUERQUE,NM 87131
[2] UNIV NEW MEXICO,DEPT CHEM & NUCL ENGN,ALBUQUERQUE,NM 87131
[3] MOTOROLA INC,MAT RES & STRATEG TECHNOL,AUSTIN,TX 78721
[4] APPL MAT INC,AUSTIN,TX 78741
关键词
CHEMICAL VAPOR DEPOSITION; COPPER; DEPOSITION PROCESS; METALLIZATION;
D O I
10.1016/0040-6090(94)05809-1
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The selective chemical vapor deposition (CVD) of Cu was studied using (hfac)Cu(VTMS) (hfac = 1,1,1,5,5,5-hexafluoroacetylacetonate; VTMS = vinyltrimethylsilane) in the absence and presence of water during CVD with SiO2 surface passivation, derived from the silylating agent hexamethyldisilazane (HMDS), as a function of the nature of the carrier gas, HMDS and water vapor flow rates and chamber pressure. For CVD of Cu in the absence of water, pre-dosing with HMDS in the absence of water gave selective deposition. The deposition was feed rate limited and dense, smooth copper films were deposited selectively at rates of about 600 Angstrom min(-1). The selectivity for CVD of Cu in the presence of water depended on the pre-dosing conditions. Pre-dosing with both HMDS and water vapor gave selective deposition at rates of about 1200 Angstrom min(-1) in the presence of water, a factor of 2 higher compared with CVD in the absence of water vapor. Dense films with near-bulk resistivities were deposited selectively in the trenches on an underlying tungsten layer at the optimum water vapor flow rate and chamber pressure. Higher water vapor flow rates and chamber pressures resulted in porous, discontinuous films with significantly higher resistivities. An integration scheme utilizing selective CVD of Cu is proposed that allows formation of fully encapsulated copper lines without the need for a copper etch.
引用
收藏
页码:52 / 59
页数:8
相关论文
共 28 条
[1]  
[Anonymous], 1979, CHEM SILICA
[2]  
Blech I. A., 1983, SOLID STATE TECH DEC, P123
[3]   ANALYSIS OF THE EFFECTS OF SCALING ON INTERCONNECT DELAY IN ULSI CIRCUITS [J].
BOTHRA, S ;
ROGERS, B ;
KELLAM, M ;
OSBURN, CM .
IEEE TRANSACTIONS ON ELECTRON DEVICES, 1993, 40 (03) :591-597
[4]   SELECTIVITY AND COPPER CHEMICAL VAPOR-DEPOSITION [J].
DUBOIS, LH ;
ZEGARSKI, BR .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1992, 139 (11) :3295-3299
[5]   FTIR STUDIES OF THE ADSORPTION/DESORPTION BEHAVIOR OF COPPER CHEMICAL-VAPOR-DEPOSITION PRECURSORS ON SILICA .1. BIS(1,1,1,5,5,5-HEXAFLUOROACETYLACETONATO)COPPER(II) [J].
FARKAS, J ;
HAMPDENSMITH, MJ ;
KODAS, TT .
JOURNAL OF PHYSICAL CHEMISTRY, 1994, 98 (27) :6753-6762
[6]   FTIR STUDIES OF THE ADSORPTION/DESORPTION BEHAVIOR OF CU CHEMICAL-VAPOR-DEPOSITION PRECURSORS ON SILICA .4. INTERACTION OF (1,1,1,5,5,5-HEXAFLUOROACETYLACETONATO)(2-BUTYNE)COPPER(I), (HFAC)CU(2-BUTYNE) AND (1,1,1,5,5,5-HEXAFLUOROACETYLACETONATO)(VINYLTRIMETHYLSILANE)COPPER(I), (HFAC)CU(VTMS) WITH PASSIVATED SILICA SURFACES AND COMPARISON TO SELECTIVE CVD OF CU [J].
FARKAS, J ;
HAMPDENSMITH, MJ ;
KODAS, TT .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1994, 141 (12) :3547-3555
[7]   FTIR STUDIES OF THE ADSORPTION/DESORPTION BEHAVIOR OF COPPER CHEMICAL-VAPOR-DEPOSITION PRECURSORS ON SILICA .2. (1,1,1,5,5,5-HEXAFLUOROACETYLACETONATO)(2-BUTYNE)COPPER(I) [J].
FARKAS, J ;
HAMPDENSMITH, MJ ;
KODAS, TT .
JOURNAL OF PHYSICAL CHEMISTRY, 1994, 98 (27) :6763-6770
[8]   FTIR STUDIES OF THE ADSORPTION/DESORPTION BEHAVIOR OF CU CHEMICAL-VAPOR-DEPOSITION PRECURSORS ON SILICA .3. REEXAMINATION OF (1,1,1,5,5,5-HEXAFLUOROACETYLACETONATO)(VINYLTRIMETHYLSILANE)COPPER(I), (HFAC)CU(VTMS) [J].
FARKAS, J ;
HAMPDENSMITH, MJ ;
KODAS, TT .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1994, 141 (12) :3539-3546
[9]   CHEMICAL-VAPOR-DEPOSITION OF COPPER FROM CU+1 PRECURSORS IN THE PRESENCE OF WATER-VAPOR [J].
GELATOS, AV ;
MARSH, R ;
KOTTKE, M ;
MOGAB, CJ .
APPLIED PHYSICS LETTERS, 1993, 63 (20) :2842-2844
[10]  
GHATE PB, 1982, THIN SOLID FILMS, V93, P359, DOI 10.1016/0040-6090(82)90143-2