SCANNING TUNNELING MICROSCOPY OF OXIDIZED TITANIUM SURFACES IN AIR

被引：13

作者：

OLIN, H

ARONSSON, BO

KASEMO, B

LAUSMAA, J

RODAHL, M

机构：

[1] Physics Department, Chalmers University of Technology

来源：

ULTRAMICROSCOPY | 1992年 / 42卷

关键词：

D O I：

10.1016/0304-3991(92)90325-E

中图分类号：

TH742 [显微镜];

学科分类号：

摘要：

Using an STM in air, we have studied three different electropolished Ti surfaces. One sample was analyzed without further treatment. The second was thermally oxidized in air at 500-degrees-C. The third was exposed to an argon glow discharge and then oxidized in pure oxygen. The samples were characterized by Auger spectroscopy prior to STM measurements. Electropolished and thermally oxidized samples showed a granular structure, with a low corrugation between 2 and 10 nm. At a larger scale, the glow discharge treated sample showed a high corrugation approximately 100 nm.

引用

页码：567 / 571

页数：5

共 21 条

[1]

ALBREKTSSON T, 1985, Critical Reviews in Biocompatibility, V1, P53

[2] MICROSTRUCTURE AND MORPHOLOGY OF SURFACE OXIDE-FILMS ON TI-6AL-4V [J].