LINEAR VISCOELASTIC DIFFUSION IN THE POLY(STYRENE)-ETHYLBENZENE SYSTEM - COMPARISON BETWEEN THEORY AND EXPERIMENT

被引:32
作者
BILLOVITS, GF [1 ]
DURNING, CJ [1 ]
机构
[1] COLUMBIA UNIV, DEPT CHEM ENGN MAT SCI & MIN, NEW YORK, NY 10027 USA
关键词
D O I
10.1021/ma00104a018
中图分类号
O63 [高分子化学(高聚物)];
学科分类号
070305 ; 080501 ; 081704 ;
摘要
We compare mutual diffusion data in the poly(styrene)-ethylbenzene system with theory. The experiments(1) were differential vapor sorptions carried out at 40 degrees C on a thin film over a range of compositions spanning the system's glass transition. Under these conditions, viscoelastic relaxation strongly influences mutual diffusion, so that non-Fickian sorption data are seen, The theories considered(2,3) account for the influence of relaxation by including fading memory in the mixture's free energy density. By fitting the data with the theory, we extracted as a function of ethylbenzene weight fraction, w(1), the mutual binary diffusion coefficient, D-12, relaxation times, tau(1) and tau(2) (>tau(1)), and the ratio of the high-frequency mechanical modulus to the osmotic modulus, k(0). In the glassy state, D-12 and tau(1) remain nearly constant, while in the liquid state they change rapidly with w(1) (D-12 increases; tau(1) decreases). The Vrentas-Duda free volume theory,(4,5) modified to account for the influence of the glass transition,(6,7) can account for the trends. The shorter relaxation time, tau(1), agrees with mechanically measured relaxation times in the transition zone.(8,9) The longer time, tau(2), shows rough agreement with the terminal time,(10,11) although the comparison is not definitive. The ratio ho is found to be constant, at similar to 0(10) over the entire concentration range, whereas the Flory-Huggins theory predicts that it should slowly increase with w(1); the reasons for the discrepancy are not clear.
引用
收藏
页码:7630 / 7644
页数:15
相关论文
共 58 条
[11]  
COLEMAN BD, 1964, ARCH RATION MECH AN, V17, P1
[12]  
Crank J, 1968, DIFFUSION POLYM
[13]   NUMERICAL INVERSION OF LAPLACE TRANSFORMS USING A FOURIER-SERIES APPROXIMATION [J].
CRUMP, KS .
JOURNAL OF THE ACM, 1976, 23 (01) :89-96
[14]  
DOI M, 1992, J PHYS II, V2, P1631, DOI 10.1051/jp2:1992225
[15]   PREDICTION OF DIFFUSION-COEFFICIENTS FOR POLYMER-SOLVENT SYSTEMS [J].
DUDA, JL ;
VRENTAS, JS ;
JU, ST ;
LIU, HT .
AICHE JOURNAL, 1982, 28 (02) :279-287
[16]   DIFFERENTIAL SORPTION IN VISCOELASTIC FLUIDS [J].
DURNING, CJ .
JOURNAL OF POLYMER SCIENCE PART B-POLYMER PHYSICS, 1985, 23 (09) :1831-1855
[17]   MUTUAL DIFFUSION IN CONCENTRATED POLYMER-SOLUTIONS UNDER A SMALL DRIVING FORCE [J].
DURNING, CJ ;
TABOR, M .
MACROMOLECULES, 1986, 19 (08) :2220-2232
[18]   UNIFIED VIEW OF TRANSPORT PHENOMENA BASED ON THE GENERALIZED BRACKET FORMULATION [J].
EDWARDS, BJ ;
BERIS, AN .
INDUSTRIAL & ENGINEERING CHEMISTRY RESEARCH, 1991, 30 (05) :873-881
[19]  
EDWARDS DA, UNPUB SIAM J APPL MA
[20]   INFLUENCE OF MOLECULAR WEIGHT AND DEGREE OF CROSSLINKING ON THE SPECIFIC VOLUME AND GLASS TEMPERATURE OF POLYMERS [J].
FOX, TG ;
LOSHAEK, S .
JOURNAL OF POLYMER SCIENCE, 1955, 15 (80) :371-390