LIMITATIONS ON THE USE OF ION-IMPLANTATION FOR THE STUDY OF THE REACTIVE ELEMENT EFFECT IN BETA-NIAL

被引:70
作者
PINT, BA [1 ]
HOBBS, LW [1 ]
机构
[1] MIT,HH UHLIG CORROS LAB,CAMBRIDGE,MA 02139
关键词
D O I
10.1149/1.2055140
中图分类号
O646 [电化学、电解、磁化学];
学科分类号
081704 ;
摘要
Numerous investigations have used the ionmimplantation of reactive elements (RE) such as Y or Ce, to study their effect on the growth of external oxide scales on alloys. Ion implanatation has, nevertheless, some specific limitations, especially in Al2O3-forming alloys. The most notable limitation occurs at temperatures > 1000-degrees-C where, owing to the shallowness of implanatation, any effects of the ion-implanted RE are short-lived and differ significantly from those observed for an RE alloy addition or an RE oxide dispersion. Additionally, in alumina-forming alloy systems, particularly beta-NiAl, implanted Y stabilizes the first-forming, metastable theta-Al2O3. The retention of the theta-Al2O3 scale on Y-implanted substrates is a chemical effect of the high concentration of Y near the substrate surface and is not a result of the implantation process itself. The loss of the RE effect at high temperatures and long times for implanted alloys is related to the outward diffusion of the RE and the formation of RE-rich oxides near the gas interface of the scale.
引用
收藏
页码:2443 / 2453
页数:11
相关论文
共 75 条
[51]  
PINT BA, UNPUB MATER HIGH TEM
[52]  
PINT BA, IN PRESS J AM CERAM
[53]   THE INFLUENCE OF YTTRIUM IMPLANTATION ON THE OXIDATION BEHAVIOR OF 67NI-33CR FE-43NI-2(CR AND FE-41NI-25CR-10AL REFRACTORY ALLOYS [J].
PIVIN, JC ;
ROQUESCARMES, C ;
CHAUMONT, J ;
BERNAS, H .
CORROSION SCIENCE, 1980, 20 (8-9) :947-962
[54]   THE FORMATION OF ALUMINUM-OXIDE SCALES ON HIGH-TEMPERATURE ALLOYS [J].
PRESCOTT, R ;
GRAHAM, MJ .
OXIDATION OF METALS, 1992, 38 (3-4) :233-254
[55]   GRAIN-BOUNDARY SEGREGATION OF YTTRIUM IN CHROMIA SCALES [J].
PRZYBYLSKI, K ;
GARRATTREED, AJ ;
YUREK, GJ .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1988, 135 (02) :509-517
[56]  
Przybylski K., 1989, Materials Science Forum, V43, P1, DOI 10.4028/www.scientific.net/MSF.43.1
[57]  
PRZYBYLSKI K, 1984, 9TH P INT C MET CORR, V1, P47
[58]   DIFFERENCES IN GROWTH MECHANISMS OF OXIDE SCALES FORMED ON ODS AND CONVENTIONAL WROUGHT ALLOYS [J].
QUADAKKERS, WJ ;
HOLZBRECHER, H ;
BRIEFS, KG ;
BESKE, H .
OXIDATION OF METALS, 1989, 32 (1-2) :67-88
[59]   COMPOSITION AND GROWTH MECHANISMS OF ALUMINA SCALES ON FECRAL-BASED ALLOYS DETERMINED BY SNMS [J].
QUADAKKERS, WJ ;
ELSCHNER, A ;
SPEIER, W ;
NICKEL, H .
APPLIED SURFACE SCIENCE, 1991, 52 (04) :271-287
[60]   THE EFFECT OF IMPLANTED YTTRIUM ON THE GROWTH AND ADHERENCE OF ALUMINA SCALES ON FE-20CR-5AL [J].
QUADAKKERS, WJ ;
JEDLINSKI, J ;
SCHMIDT, K ;
KRASOVEC, M ;
BORCHARDT, G ;
NICKEL, H .
APPLIED SURFACE SCIENCE, 1991, 47 (03) :261-272