GROWTH OF HIGHLY ORIENTED TIN OXIDE THIN-FILMS BY LASER EVAPORATION DEPOSITION

被引:45
作者
DAI, CM
SU, CS
CHUU, DS
机构
[1] NATL TSING HUA UNIV,INST NUCL SCI,HSINCHU 300,TAIWAN
[2] NATL CHIAO TUNG UNIV,DEPT ELECTROPHYS,HSINCHU,TAIWAN
关键词
D O I
10.1063/1.103998
中图分类号
O59 [应用物理学];
学科分类号
摘要
Conducting and transparent thin films of tin oxide were prepared by the laser evaporation of an undoped powder-pressed polycrystalline tin oxide target onto unheated substrates. After characterizing these films, the results reveal that the films are highly oriented and with a grain size ∼0.2 μm. The nearly stoichiometric deposition of tin oxide films with deposition rates exceeding 24 Å per pulse was obtained by this method. The lowest resistivity obtained is 3.0×10-3 Ω cm. The visible transmittance (between 4000 and 7000 Å) is above 75%.
引用
收藏
页码:1879 / 1881
页数:3
相关论文
共 16 条
  • [11] SPRAYED FILMS OF INDIUM TIN OXIDE AND FLUORINE-DOPED TIN OXIDE OF LARGE SURFACE-AREA
    POMMIER, R
    GRIL, C
    MARUCCHI, J
    [J]. THIN SOLID FILMS, 1981, 77 (1-3) : 91 - 97
  • [12] EPITAXIAL-GROWTH OF YBA2CU3O7-X THIN-FILMS BY A LASER EVAPORATION PROCESS
    ROAS, B
    SCHULTZ, L
    ENDRES, G
    [J]. APPLIED PHYSICS LETTERS, 1988, 53 (16) : 1557 - 1559
  • [13] X-RAY-DIFFRACTION ANALYSIS OF SNO2 FILMS PREPARED BY OXIDATION OF TIN FILMS
    SINHA, NP
    MISRA, M
    [J]. THIN SOLID FILMS, 1983, 101 (02) : L33 - L34
  • [14] TRANSPARENT CONDUCTING SNOX FILMS HIGH-RATE REACTIVELY SPUTTERED ONTO POLYESTER FOIL
    STJERNA, B
    GRANQVIST, CG
    [J]. APPLIED OPTICS, 1990, 29 (04): : 447 - 448
  • [15] STRUCTURAL, ELECTRICAL AND OPTICAL-PROPERTIES OF RF-MAGNETRON-SPUTTERED SNO2-SB FILM
    SUZUKI, K
    MIZUHASHI, M
    [J]. THIN SOLID FILMS, 1982, 97 (02) : 119 - 127
  • [16] LOW-TEMPERATURE GROWTH OF TRANSPARENT AND CONDUCTING TIN OXIDE FILM BY PHOTOCHEMICAL VAPOR-DEPOSITION
    TABUCHI, T
    YAMAGISHI, K
    TARUI, Y
    [J]. JAPANESE JOURNAL OF APPLIED PHYSICS PART 2-LETTERS, 1987, 26 (03): : L186 - L189