Effects of the morphology and structure on the elastic behavior of (Ti,Si,Al)N nanocomposites

被引:40
作者
Carvalho, S
Ribeiro, E
Rebouta, L
Vaz, F
Alves, E
Schneider, D
Cavaleiro, A
机构
[1] Univ Minho, Dept Fis, P-4800058 Guimaraes, Portugal
[2] ITN, Dept Fis, P-2686953 Sacavem, Portugal
[3] Fraunhofer Inst Mat Beam Technol, D-01277 Dresden, Germany
[4] Univ Coimbra, Fac Ciencias & Tecnol, ICMES, P-3030 Coimbra, Portugal
关键词
Ti-Si-Al-N; nanocomposite; Young's modulus; SEM; morphology; porosity;
D O I
10.1016/S0257-8972(03)00386-4
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
(Ti,Si,Al)N nanocomposite coatings with different Ti, Si, Al contents, were deposited onto silicon and polished high-speed steel substrates, by r.f. and/or d.c. reactive magnetron sputtering. The stoichiometry of the films was investigated by electron probe microanalysis and Rutherford backscattering spectrometry (RBS). The density was derived by combination of RBS results and thickness measurements obtained by ball-cratering. For comparison purposes, the evaluation of the Young's modulus was performed by depth-sensing indentation technique and with the laser-acoustic technique based on surface acoustic waves (SAW). Results showed in some cases differences in Young's modulus measured by both techniques. The Young's modulus obtained by SAW correlates with the density values from RBS, however, this behavior is not visible for the results measured with the ultramicroindentation technique. Both techniques indicate a small increase of Young's modulus of (Ti,AI)N by incorporating Si into the matrix. However, this improvement only occurs for small Si content, whereas for high Si content the elastic parameter reduces until almost 300 GPa. The morphology of the coatings was investigated by scanning electron microscopy and correlated with the differences observed by both SAW and indentation techniques. (C) 2003 Elsevier Science B.V. All rights reserved.
引用
收藏
页码:984 / 991
页数:8
相关论文
共 48 条
[11]   Gathering data on materials resistant to wear [J].
Friedrich, C ;
Berg, G ;
Broszeit, E ;
Berger, C .
MATERIALWISSENSCHAFT UND WERKSTOFFTECHNIK, 1997, 28 (02) :59-76
[13]  
Hauert R, 2000, ADV ENG MATER, V2, P247, DOI 10.1002/(SICI)1527-2648(200005)2:5<247::AID-ADEM247>3.0.CO
[14]  
2-U
[15]  
Hertzberg RW., 2012, Deformation and fracture mechanics of engineering materials, copy right © 1976, 1983, V5th
[16]   THE HARDNESS AND YOUNG MODULUS OF AMORPHOUS HYDROGENATED CARBON AND SILICON FILMS MEASURED WITH AN ULTRALOW LOAD INDENTER [J].
JIANG, X ;
REICHELT, K ;
STRITZKER, B .
JOURNAL OF APPLIED PHYSICS, 1989, 66 (12) :5805-5808
[17]   ELASTIC-CONSTANTS AND HARDNESS OF ION-BEAM-SPUTTERED TINX FILMS MEASURED BY BRILLOUIN-SCATTERING AND DEPTH-SENSING INDENTATION [J].
JIANG, X ;
WANG, M ;
SCHMIDT, K ;
DUNLOP, E ;
HAUPT, J ;
GISSLER, W .
JOURNAL OF APPLIED PHYSICS, 1991, 69 (05) :3053-3057
[18]  
KELLY A, 1986, STRONG MAT
[19]   Elastic modulus of plasma-sprayed coatings determined by indentation and bend tests [J].
Kim, HJ ;
Kweon, YG .
THIN SOLID FILMS, 1999, 342 (1-2) :201-206
[20]  
KLUG HP, 1974, XRAY DIFFRACTION PRO, pCH9