Piezoelectric properties of Ca-modified PbTiO3 thin films

被引:94
作者
Kholkin, AL [1 ]
Calzada, ML [1 ]
Ramos, P [1 ]
Mendiola, J [1 ]
Setter, N [1 ]
机构
[1] CSIC,ICMM,DEPT MET FERROELECT,E-28049 MADRID,SPAIN
关键词
D O I
10.1063/1.117220
中图分类号
O59 [应用物理学];
学科分类号
摘要
Low-field piezoelectric coefficient and strain were investigated in Ca-modified PbTiO3 thin films by means of optical interferometry. A remanent piezoelectric coefficient of 70 pm/V was observed that agrees well with the values previously reported for the bulk ceramics of the same composition. The efficient poling of the films can be achieved at room temperature under the held of 300 kV/cm. Electrically induced strains as high as 0.8% were observed using a bipolar driving field of 1 MV/cm. Strain response under a unipolar driving field exhibited a good linearity and small hysteresis. These properties combined with the low dielectric constant and high dielectric strength are shown to be attractive for micromechanical applications. (C) 1996 American Institute of Physics.
引用
收藏
页码:3602 / 3604
页数:3
相关论文
共 21 条
  • [1] Processing parameters affecting the properties of sol-gel-derived modified lead titanate thin films
    Calzada, ML
    Mendiola, J
    Carmona, F
    Ramos, P
    Sirera, R
    [J]. MATERIALS RESEARCH BULLETIN, 1996, 31 (04) : 413 - 421
  • [2] ELECTRICAL-PROPERTIES MAXIMA IN THIN-FILMS OF THE LEAD ZIRCONATE LEAD TITANATE SOLID-SOLUTION SYSTEM
    CHEN, HD
    UDAYAKUMAR, KR
    GASKEY, CJ
    CROSS, LE
    [J]. APPLIED PHYSICS LETTERS, 1995, 67 (23) : 3411 - 3413
  • [3] DAMJANOVIC D, 1995, MATER RES SOC SYMP P, V360, P429
  • [4] DAMJANOVIC D, 1987, AM CERAM SOC BULL, V66, P699
  • [5] EVOLUTION OF THE SPATIAL-DISTRIBUTION OF POLARIZATION IN LEAD-CALCIUM FERROELECTRIC CERAMICS
    DEFRUTOS, J
    JIMENEZ, B
    [J]. FERROELECTRICS, 1992, 126 (1-4) : 341 - 345
  • [6] PIEZOELECTRIC PROPERTIES OF SOL GEL-DERIVED SAMARIUM-DYSPROSIUM-MODIFIED LEAD TITANATE CERAMICS
    HAYES, JM
    GURURAJA, TR
    CROSS, LE
    GEOFFROY, GL
    [J]. JOURNAL OF MATERIALS SCIENCE, 1988, 23 (06) : 2087 - 2092
  • [7] Jaffe B., 1971, PIEZOELECTRIC CERAMI
  • [8] Interferometric measurements of electric field-induced displacements in piezoelectric thin films
    Kholkin, AL
    Wutchrich, C
    Taylor, DV
    Setter, N
    [J]. REVIEW OF SCIENTIFIC INSTRUMENTS, 1996, 67 (05) : 1935 - 1941
  • [9] MEASUREMENT OF PIEZOELECTRIC COEFFICIENTS OF FERROELECTRIC THIN-FILMS
    LEFKI, K
    DORMANS, GJM
    [J]. JOURNAL OF APPLIED PHYSICS, 1994, 76 (03) : 1764 - 1767
  • [10] PIEZOELECTRIC PROPERTIES OF SOL-GEL-DERIVED FERROELECTRIC AND ANTIFERROELECTRIC THIN-LAYERS
    LI, JF
    VIEHLAND, DD
    TANI, T
    LAKEMAN, CDE
    PAYNE, DA
    [J]. JOURNAL OF APPLIED PHYSICS, 1994, 75 (01) : 442 - 448