Melt-processable thermosetting polyimide: Synthesis, characterization, fusibility, and property

被引：35

作者：

Kuroki, T ^{[1
]}

Shibuya, A ^{[1
]}

Toriida, M ^{[1
]}

Tamai, S ^{[1
]}

机构：

[1] Mitsui Chem Inc, Mat Sci Lab, Adv Mat Grp, Sodegaura, Chiba 2990265, Japan

来源：

JOURNAL OF POLYMER SCIENCE PART A-POLYMER CHEMISTRY | 2004年 / 42卷 / 10期

关键词：

thermosets; polyimides; synthesis; molding;

D O I：

10.1002/pola.20079

中图分类号：

O63 [高分子化学（高聚物）];

学科分类号：

070305 ; 080501 ; 081704 ;

摘要：

To obtain a melt-processable thermosetting polyimide having a high glasstransition temperature (T,,) and good solvent resistance, the effect of introducing a crosslinkable agent into the polymer chain ends of the melt-processable polyimide on its physical properties was studied. The polyimide (calculated number-average molecular weight (M-n) = 11,600 g/mol) capped with the crosslinkable agent exhibited poor melt flowability because its crosslinkable agent reacted at the processing temperature of 360 degreesC. To reduce the rate of crosslink reaction, two methods were investigated. One was lowering the processing temperature, and the other was decreasing the amount of crosslinkable agent. The low-molecular-weight oligomer (calculated M-n = 6300 g/mol) capped with the crosslinkable agent exhibited good melt flowability at the lower processing temperature of 340 degreesC where the crosslinkable agent did not react. However, the obtained molded part of this oligomer was too brittle to maintain its shape. However, the polyimide (calculated . = 11,600 g/mol) partially capped with the crosslinkable agent demonstrated good melt flowability at the processing temperature of 360 degreesC. Furthermore, the molded part of this resin was strong and tough. In addition, the cured part exhibited high T-g, and good solvent resistance. (C) 2004 Wiley Periodicals, Inc.

引用

页码：2395 / 2404

页数：10

共 27 条

[21]

Mittal KL, 1984, POLYIMIDES SYNTHESIS, V1

[22]

OHTA M, 1989, Patent No. 4847349

[23] Synthesis and characterization of thermally stable semicrystalline polyimide based on 3,4′-oxydianiline and 3,3′,4,4′-biphenyltetracarboxylic dianhydride [J].

Tamai, S ;

Kuroki, T ;

Shibuya, A ;

Yamaguchi, A .

POLYMER, 2001, 42 (06) :2373-2378

[24] Melt processable copolyimides based on 4,4′-bis(3-aminophenoxy)biphenyl [J].

Tamai, S ;

Oikawa, H ;

Ohta, M ;

Yamaguchi, A .

POLYMER, 1998, 39 (10) :1945-1949

[25] Melt processible polyimides and their chemical structures [J].

Tamai, S ;

Yamaguchi, A ;

Ohta, M .

POLYMER, 1996, 37 (16) :3683-3692

[26]

Wilson D., 1990, POLYIMIDES

[27] Molecular design of heat resistant polyimides having excellent processability and high glass transition temperature [J].

Yokota, R ;

Yamamoto, S ;

Yano, S ;

Sawaguchi, T ;

Hasegawa, M ;

Yamaguchi, H ;

Ozawa, H ;

Sato, R .

HIGH PERFORMANCE POLYMERS, 2001, 13 (02) :S61-S72

← 1 2 3 →