Effect of Ni layer thickness and soldering time on intermetallic compound formation at the interface between molten Sn-3.5Ag and Ni/Cu substrate

被引:73
作者
Choi, WK [1 ]
Lee, HM [1 ]
机构
[1] Korea Adv Inst Sci & Technol, Dept Mat Sci & Engn, Taejon 305701, South Korea
关键词
Ni layer thickness; eutectic Sn-3.5wt.%Ag alloy; Ni-Cu substrate;
D O I
10.1007/s11664-999-0164-1
中图分类号
TM [电工技术]; TN [电子技术、通信技术];
学科分类号
0808 ; 0809 ;
摘要
The binary eutectic Sn-3.5wt.%Ag alloy was soldered on the Ni/Cu plate at 250 degrees C, the thickness of the Ni layer changing from 0 through 2 and 4 mu m to infinity, and soldering time changing from 30 to 120 s at intervals of 30 s. The infinite thickness was equivalent to the bare Ni plate. The morphology, composition and phase identification of the intermetallic compound (IMC, hereafter) formed at the interface were examined. Depending on the initial Ni thickness, different IMC phases were observed at 30 s: Cu6Sn5 on bare Cu, metastable NiSn3 + Ni3Sn4 on Ni(2 mu m)lCu, Ni3Sn4 on Ni(4 mu m)/Cu, and Ni3Sn + Ni3Sn4 on bare Ni. With increased soldering time, a Cu-Sn-based eta-(Cu6Sn5)(1-x)Ni-x phase formed under the pre-formed Ni-Sn IMC layer both at 60 s in the Ni(2 mu m)/Cu plate and at 90 s in the Ni(4 mu m)/Cu plate. The two-layer IMC pattern remained thereafter. The wetting behavior of each joint was different and it may have resulted from the type of IMC formed on each plate. The thickness of the protective Ni layer over the Cu plate was found to be an important factor in determining the interfacial reaction and the wetting behavior.
引用
收藏
页码:1251 / 1255
页数:5
相关论文
共 27 条
[1]   RAPID FORMATION OF INTERMETALLIC COMPOUNDS BY INTERDIFFUSION IN THE CU-SN AND NI-SN SYSTEMS [J].
BADER, S ;
GUST, W ;
HIEBER, H .
ACTA METALLURGICA ET MATERIALIA, 1995, 43 (01) :329-337
[2]  
BADER WG, 1969, WELDING RES S, V48, P551
[3]   Electric current effects upon the Sn/Cu and Sn/Ni interfacial reactions [J].
Chen, SW ;
Chen, CM ;
Liu, WC .
JOURNAL OF ELECTRONIC MATERIALS, 1998, 27 (11) :1193-1198
[4]  
Fontana M., 1987, CORROSION ENG, V3rd
[5]   Thermodynamic modeling of the palladium-lead-tin system [J].
Ghosh, G .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1999, 30 (01) :5-18
[6]   MICROSTRUCTURE AND MECHANICAL-PROPERTIES OF PB-FREE SOLDER ALLOYS FOR LOW-COST ELECTRONIC ASSEMBLY - A REVIEW [J].
GLAZER, J .
JOURNAL OF ELECTRONIC MATERIALS, 1994, 23 (08) :693-700
[7]  
HAIMOVICH J, 1989, WELDING J RES S, V8, pS101
[8]   DEVELOPING LEAD-FREE SOLDERS - A CHALLENGE AND OPPORTUNITY [J].
JIN, SH .
JOM-JOURNAL OF THE MINERALS METALS & MATERIALS SOCIETY, 1993, 45 (07) :13-13
[9]   GROWTH-KINETICS OF INTERMETALLIC PHASES AT THE LIQUID SN AND SOLID NI INTERFACE [J].
KANG, SK ;
RAMACHANDRAN, V .
SCRIPTA METALLURGICA, 1980, 14 (04) :421-424
[10]   Interfacial reactions during soldering with lead-tin eutectic and lead (Pb)-free, tin-rich solders [J].
Kang, SK ;
Rai, RS ;
Purushothaman, S .
JOURNAL OF ELECTRONIC MATERIALS, 1996, 25 (07) :1113-1120