OPTICAL-CONSTANTS AND FILM DENSITY OF TINXOY SOLAR SELECTIVE ABSORBERS

被引:58
作者
LAZAROV, M
RATHS, P
METZGER, H
SPIRKL, W
机构
[1] Ludwig-Maximilians-Universität, Sektion Physik, D-80799 Munich
关键词
D O I
10.1063/1.358790
中图分类号
O59 [应用物理学];
学科分类号
摘要
Thin TiNxOy films were deposited on glass substrates in an activated reactive evaporation process. The influence of the reactive gas composition and pressure during deposition on the film density ρMass was investigated by grazing incidence x-ray-diffraction measurements. The density increases from 3.8 to 4.8 g/cm3 when lowering the total gas pressure ptotal from 10-3 h Pa down to 2.5×10-4 h Pa, whereas the ratio of the partial gas pressures of nitrogen and oxygen has no measurable effect on the film density. Data on the refractive index are presented, obtained from reflectance and transmittance measurements in the optical wavelength range (λ=0.3-2.5 μm). Bruggeman effective medium theory was applied to explain the optical behavior ñ(λ) as a result of the low density of the coatings. The high porosity of the films suppresses the metallic character of the phases TiN and TiO contained in the TiNxOy film. Its dielectriclike behavior in the infrared region is essential for low thermal emittances when deposited on copper to form a solar selective absorber. © 1995 American Institute of Physics.
引用
收藏
页码:2133 / 2137
页数:5
相关论文
共 27 条
[1]  
[Anonymous], 1976, OPTICS THIN FILMS OP
[2]   OPTICAL-PROPERTIES OF THIN-FILMS [J].
ASPNES, DE .
THIN SOLID FILMS, 1982, 89 (03) :249-262
[3]   MATERIALS FOR PHOTOTHERMAL SOLAR-ENERGY CONVERSION [J].
BOGAERTS, WF ;
LAMPERT, CM .
JOURNAL OF MATERIALS SCIENCE, 1983, 18 (10) :2847-2875
[4]   ACTIVATED REACTIVE EVAPORATION PROCESS FOR HIGH RATE DEPOSITION OF COMPOUNDS [J].
BUNSHAH, RF ;
RAGHURAM, AC .
JOURNAL OF VACUUM SCIENCE & TECHNOLOGY, 1972, 9 (06) :1385-&
[5]   COMPARISON OF SEVERAL SHORTWAVE PASS FILTER DESIGNS [J].
CARNIGLIA, CK .
APPLIED OPTICS, 1989, 28 (14) :2820-2823
[6]   CONCENTRATION PROFILING USING X-RAY REFLECTIVITY - APPLICATION TO CU-AL INTERFACES [J].
CHEN, H ;
HEALD, SM .
JOURNAL OF APPLIED PHYSICS, 1989, 66 (04) :1793-1799
[7]   OPTIMIZATION OF INTERFERENCE FILTERS WITH GENETIC ALGORITHMS APPLIED TO SILVER-BASED HEAT MIRRORS [J].
EISENHAMMER, T ;
LAZAROV, M ;
LEUTBECHER, M ;
SCHOFFEL, U ;
SIZMANN, R .
APPLIED OPTICS, 1993, 32 (31) :6310-6315
[8]  
EITLE J, 1992, P SOC PHOTO-OPT INS, V1727, P25, DOI 10.1117/12.130486
[9]   LOW-TEMPERATURE OXIDATION BEHAVIOR OF REACTIVELY SPUTTERED TIN BY X-RAY PHOTOELECTRON-SPECTROSCOPY AND CONTACT RESISTANCE MEASUREMENTS [J].
ERNSBERGER, C ;
NICKERSON, J ;
SMITH, T .
JOURNAL OF VACUUM SCIENCE & TECHNOLOGY A-VACUUM SURFACES AND FILMS, 1986, 4 (06) :2784-2788
[10]   OPTICAL-PROPERTIES OF CVD-COATED TIN, ZRN AND HFN [J].
KARLSSON, B ;
SHIMSHOCK, RP ;
SERAPHIN, BO ;
HAYGARTH, JC .
SOLAR ENERGY MATERIALS, 1983, 7 (04) :401-411