CORROSION AND PASSIVATION OF AL AND AL-SI ALLOYS IN NITRIC-ACID SOLUTIONS .2. EFFECT OF CHLORIDE-IONS

被引:57
作者
ALKHARAFI, FM [1 ]
BADAWY, WA [1 ]
机构
[1] KUWAIT UNIV,FAC SCI,DEPT CHEM,SAFAT 13060,KUWAIT
关键词
CORROSION; PASSIVATION; ALUMINUM; ALUMINUM ALLOYS; ELECTROCHEMICAL IMPEDANCE SPECTROSCOPY;
D O I
10.1016/0013-4686(95)00091-R
中图分类号
O646 [电化学、电解、磁化学];
学科分类号
081704 ;
摘要
The electrochemical behaviour of aluminium and Al-silicon alloys in aqueous solutions containing different concentrations of chloride ions was investigated. Electrochemical impedance spectroscopy (EIS) and polarization techniques were used. The electrodes were anodically passivated under galvanostatic control. The effect of formation voltage on the stability of the passive film was studied. The open-circuit impedance measurements have shown that the dissolution of the anodic oxide formed on aluminium or aluminium alloys follows the empirical relation: C-1 = C-0(-1) - Bt(1/2) C-1 is proportional to the oxide film thickness. B represents the rate coefficient of the oxide film dissolution. The results revealed that the presence of chloride ions even in the oxidizing medium (1 M HNO3) delays the passivation of the material. Complex plane analysis of the formed oxide film indicates that the corrosion resistance increases as the concentration of chloride ions increases. For naturally passivated electrodes, the corrosion resistance decreases as the concentration of chloride ions increases. This behaviour was explained by film repair-film removal equilibria.
引用
收藏
页码:1811 / 1817
页数:7
相关论文
共 30 条
[1]   ANODIZATION AND BREAKDOWN MODEL OF TA2O5 FILMS [J].
ALBELLA, JM ;
MONTERO, I ;
MARTINEZDUART, JM .
THIN SOLID FILMS, 1985, 125 (1-2) :57-62
[2]  
BADAWY WA, 1986, INDIAN J TECHNOL, V24, P1
[3]   KINETIC-STUDIES ON THE DISSOLUTION BEHAVIOR OF ANODIC OXIDE-FILMS ON ALUMINUM IN KF-SOLUTIONS [J].
BADAWY, WA ;
IBRAHIM, MM ;
ABOUROMIA, MM ;
ELBASIOUNY, MS .
CORROSION, 1986, 42 (06) :324-328
[4]   ELECTROCHEMICAL IMPEDANCE SPECTROSCOPIC INVESTIGATION OF TANTALUM AND ITS PASSIVE FILMS IN ACIDIC AND NEUTRAL SOLUTIONS [J].
BADAWY, WA ;
ISMAIL, KM .
ELECTROCHIMICA ACTA, 1993, 38 (15) :2231-2237
[5]  
BADAWY WA, UNPUB J APPL ELECTRO
[6]   INFLUENCE OF HYDROSTATIC-PRESSURE AND SALT CONCENTRATION ON ALUMINUM CORROSION IN NACL SOLUTIONS [J].
BECCARIA, AM ;
POGGI, G .
CORROSION, 1986, 42 (08) :470-475
[7]   AC-IMPEDANCE MEASUREMENTS ON ALUMINUM BARRIER TYPE OXIDE-FILMS [J].
BESSONE, J ;
MAYER, C ;
JUTTNER, K ;
LORENZ, WJ .
ELECTROCHIMICA ACTA, 1983, 28 (02) :171-175
[8]  
BESSONE JB, 1981, 8TH P ICMC MAINZ, V1, P229
[9]  
BREITER MW, 1970, ELECTROCHIM ACTA, V15, P1145
[10]   THE APPLICATION OF ELECTROCHEMICAL IMPEDANCE TECHNIQUES TO ALUMINUM CORROSION IN ACIDIC CHLORIDE SOLUTION [J].
BRETT, CMA .
JOURNAL OF APPLIED ELECTROCHEMISTRY, 1990, 20 (06) :1000-1003