ELIMINATION OF DISLOCATIONS IN HETEROEPITAXIAL MBE AND RTCVD GEXSI1-X GROWN ON PATTERNED SI SUBSTRATES

We have grown Ge x Si1-x (0 <x < 0.20,1000-3000Å thick) on small growth areas etched in the Si substrate. Layers were grown using both molecular beam epitaxy (MBE) at 550° C and rapid thermal chemical vapor deposition (RTCVD) at 900° C. Electron beam induced current images (EBIC) (as well as defect etches and transmission electron microscopy) show that 2800Å-thick, MBE Ge0.19Si0.81 on 70-μm-wide mesas have zerothreading and nearly zero misfit dislocations. The Ge0.19Si{0.81} grown on unpatterned, large areas is heavily dislocated. It is also evident from the images that heterogeneous nucleation of misfit dislocations is dominant in this composition range. 1000Å-thick, RTCVD Ge0.14Si0.86 films deposited on 70 μm-wide mesas are also nearly dislocation-free as shown by EBIC, whereas unpatterned areas are more heavily dislocated. Thus, despite the high growth temperatures, only heterogeneous nucleation of misfit dislocations occurs and patterning is still effective. Photoluminescence spectra from arrays of GeSi on Si mesas show that even when the interface dislocation density on the mesas is high, growth on small areas results in a lower dislocation density than growth on large areas. © 1990 AIME.