EFFECTS OF TARGET AND TEMPLATE LAYER ON THE PROPERTIES OF HIGHLY CRYSTALLINE SUPERCONDUCTING A-AXIS FILMS OF Y1BA2CU3O7-X BY DC-SPUTTERING

被引：21
作者：
MAHAJAN, S
ITO, W
YOSHIDA, Y
MORISHITA, T
机构：
[1] Superconductivity Research Laboratory, ISTEC, Koto-ku, Tokyo, 135, 10-13 Shinonome
来源：
PHYSICA C | 1993年 / 213卷 / 3-4期
关键词：
D O I：
10.1016/0921-4534(93)90465-3
中图分类号：
O59 [应用物理学];
学科分类号：
摘要：
Highly crystalline superconducting a-axis oriented thin films of Y1Ba2Cu3O7-x were prepared using the template layer method on SrTiO3, MgO and NdGaO3 substrates by DC-sputtering in the on-axis configuration. A full width at half maximum value of 0.05-degrees was measured through the rocking curve of the (200) film peak on SrTiO3. The films had a very smooth surface morphology with no particles as revealed by scanning electron microscopy and a critical onset temperature above 84 K. Critical current density as measured by magnetic hysteresis measurements was found to be inversely related to the crystallinity of the film. The characteristics of the resulting films were largely dependent on the target used, mainly on the activated oxygen released from the target. The effects of template layer and substrate biasing on the crystalline and superconducting properties of a-axis films are discussed.
引用
收藏
页码：445 / 454
页数：10
相关论文
共 9 条
[1]   MAGNETIZATION OF HARD SUPERCONDUCTORS [J].
BEAN, CP .
PHYSICAL REVIEW LETTERS, 1962, 8 (06) :250-+
[2]   CRITICAL PARAMETERS IN THE SINGLE-TARGET SPUTTERING OF YBA2CU3O7 [J].
GAVALER, JR ;
TALVACCHIO, J ;
BRAGGINS, TT ;
FORRESTER, MG ;
GREGGI, J .
JOURNAL OF APPLIED PHYSICS, 1991, 70 (08) :4383-4391
[3]   A-AXIS ORIENTED YBA2CU3O7 SUPERCONDUCTING THIN-FILM GROWN ON MGO SUBSTRATE [J].
HAMET, JF ;
MERCEY, B ;
HERVIEU, M ;
RAVEAU, B .
PHYSICA C, 1992, 193 (3-4) :465-470
[4]   PHASE CHARACTERIZATION OF DYSPROSIUM BARIUM COPPER-OXIDE THIN-FILMS GROWN ON STRONTIUM-TITANATE BY MOLECULAR-BEAM EPITAXY [J].
HELLMAN, ES ;
SCHLOM, DG ;
MARSHALL, AF ;
STREIFFER, SK ;
HARRIS, JS ;
BEASLEY, MR ;
BRAVMAN, JC ;
GEBALLE, TH ;
ECKSTEIN, JN ;
WEBB, C .
JOURNAL OF MATERIALS RESEARCH, 1989, 4 (03) :476-495
[5]   A-AXIS ORIENTED EPITAXIAL YBA2CU3O7-X-PRBA2CU3O7-Y HETEROSTRUCTURES [J].
INAM, A ;
ROGERS, CT ;
RAMESH, R ;
REMSCHNIG, K ;
FARROW, L ;
HART, D ;
VENKATESAN, T ;
WILKENS, B .
APPLIED PHYSICS LETTERS, 1990, 57 (23) :2484-2486
[6]   HIGHEST CRYSTALLINITY OF A-AXIS YBCO FILMS BY DC-94.92 MHZ HYBRID PLASMA MAGNETRON SPUTTERING [J].
ITO, W ;
OISHI, A ;
OKAYAMA, S ;
YOSHIDA, Y ;
HOMMA, N ;
MORISHITA, T ;
HAGA, T ;
YAMAYA, K .
PHYSICA C, 1993, 204 (3-4) :295-298
[7]  
ITO W, UNPUB PHYSICA C
[8]   OXYGEN-CONTENT AND DISORDER IN A-AXIS ORIENTED YBA2CU3O7-DELTA THIN-FILMS [J].
SODTKE, E ;
MUNDER, H .
APPLIED PHYSICS LETTERS, 1992, 60 (13) :1630-1632
[9]   THE INFLUENCE OF THE TEMPLATE GROWTH METHOD ON THE PROPERTIES OF A-AXIS ORIENTED YBA2CU3O7-DELTA THIN-FILMS [J].
SODTKE, E ;
MUNDER, H ;
BRAGINSKI, AI .
PHYSICA C, 1993, 204 (3-4) :375-383
1