LASER NITRIDING OF IRON - NITROGEN PROFILES AND PHASES

被引：19

作者：

ILLGNER, C ^{[1
]}

SCHAAF, P ^{[1
]}

LIEB, KP ^{[1
]}

SCHUBERT, E ^{[1
]}

QUEITSCH, R ^{[1
]}

BERGMANN, HW ^{[1
]}

机构：

[1] APPLIKAT & TECH ZENTRUM EVUS,D-92249 VILSECK,GERMANY

来源：

APPLIED PHYSICS A-MATERIALS SCIENCE & PROCESSING | 1995年 / 61卷 / 01期

关键词：

D O I：

10.1007/BF01538202

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Armco iron samples were surface nitrided by irradiating them with pulses of an excimer laser in a nitrogen atmosphere, The resulting nitrogen depth profiles measured by Resonant Nuclear Reaction Analysis (RNRA) and the phase formation determined by Conversion Electron Mossbauer Spectroscopy (GEMS) were investigated as functions of energy density and the number of pulses. The nitrogen content of the samples was found to be independent of the number of pulses in a layer of 50 nm from the surface and to increase in depths exceeding 150 nm, The phase composition did not change with the number of pulses. The nitrogen content can be related to an enhanced nitrogen solubility based on high temperatures and high pressures due to the laser-induced plasma above the sample. With increasing pulse energy density, the phase composition changes towards phases with higher nitrogen contents. Nitrogen diffusion seems to be the limiting factor for the nitriding process.

引用

页码：1 / 5

页数：5

共 28 条

[21]

UGLOV AA, 1989, J PHYS-PARIS, V50, pC5

[22] ENERGY CALIBRATION OF THE 500 KV HEAVY-ION IMPLANTER IONAS [J].