THE MECHANISM OF ELECTROMIGRATION FAILURE OF NARROW AL-2CU-1SI THIN-FILM INTERCONNECTS

被引:32
作者
KIM, CG [1 ]
MORRIS, JW [1 ]
机构
[1] UNIV CALIF BERKELEY, DEPT MAT SCI, BERKELEY, CA 94720 USA
关键词
D O I
10.1063/1.353806
中图分类号
O59 [应用物理学];
学科分类号
摘要
This work is principally concerned with the microstructure of electromigration failure in narrow Al-2Cu-1Si conducting lines on Si. Samples were patterned from 0.5-mum-thick vapor-deposited films with mean grain size of 2.4 mum, and had linewidths of 1.3 mum (W/G almost-equal-to 0.5), 2 mum (W/G almost-equal-to 0.8), and 6 mum (W/G almost-equal-to 2.5). The lines were tested to failure at T=226-degrees-C and j=2.5X10(6) mu/cm2. Other samples were tested over a range of substrate temperatures and current densities to test the effect of these variables, and 1.3 mum lines were tested after preaging at 226-degrees-C for various times to change the Cu-precipitate distribution prior to testing. Three failure modes were observed: The 6 mum specimens failed by separation along grain boundaries with an apparent activation energy of 0.65 eV; the 1.3 mum specimens that were preaged for 24 h failed after very long times by gradual thinning to rupture; all other narrow lines failed by the transgranular-slit mechanism with an activation energy near 0.93 eV. Microstructural studies suggest that the transgranular-slit failure mechanism is due to the accumulation of a supersaturation of vacancies in the bamboo grains that terminate polygranular segments in the line. Failure occurs after Cu has been swept from the grain that fails. Failure happens first at the end of the longest polygranular segment of the line, at a time that decreases exponentially with the polygranular segment length. Preaging the line to create a more stable distribution of Cu lengthens the time required to sweep Cu from the longest polygranular segment, and significantly increases the time to failure. In the optimal case the transgranular-slit failure mechanism is suppressed, and the bamboo grain fails by diffuse thinning to rupture. Preaging is particularly effective in increasing the lifetimes of lines that contain very long polygranular segments, and has the consequence that the time to first failure in an array of lines is much longer than predicted by a log-normal fit to the distribution of failure times.
引用
收藏
页码:4885 / 4893
页数:9
相关论文
共 33 条
[1]   A MODEL FOR THE EFFECT OF LINE-WIDTH AND MECHANICAL STRENGTH ON ELECTROMIGRATION FAILURE OF INTERCONNECTS WITH NEAR-BAMBOO GRAIN STRUCTURES [J].
ARZT, E ;
NIX, WD .
JOURNAL OF MATERIALS RESEARCH, 1991, 6 (04) :731-736
[2]   ELECTROMIGRATION DAMAGE IN ALUMINUM FILM CONDUCTORS [J].
ATTARDO, MJ ;
ROSENBERG, R .
JOURNAL OF APPLIED PHYSICS, 1970, 41 (06) :2381-+
[3]   STRESS GENERATION BY ELECTROMIGRATION [J].
BLECH, IA ;
HERRING, C .
APPLIED PHYSICS LETTERS, 1976, 29 (03) :131-133
[4]   ELECTROMIGRATION IN THIN ALUMINUM FILMS ON TITANIUM NITRIDE [J].
BLECH, IA .
JOURNAL OF APPLIED PHYSICS, 1976, 47 (04) :1203-1208
[5]   GRAIN-SIZE DEPENDENCE OF ELECTROMIGRATION-INDUCED FAILURES IN NARROW INTERCONNECTS [J].
CHO, J ;
THOMPSON, CV .
APPLIED PHYSICS LETTERS, 1989, 54 (25) :2577-2579
[6]   ELECTROMIGRATION-INDUCED FAILURES IN INTERCONNECTS WITH BIMODAL GRAIN-SIZE DISTRIBUTIONS [J].
CHO, J ;
THOMPSON, CV .
JOURNAL OF ELECTRONIC MATERIALS, 1990, 19 (11) :1207-1212
[7]   KINETICS OF VACANCY MOTION IN HIGH-PURITY ALUMINUM [J].
DESORBO, W ;
TURNBULL, D .
PHYSICAL REVIEW, 1959, 115 (03) :560-563
[8]   EFFECT OF COPPER ADDITIONS ON ELECTROMIGRATION IN ALUMINUM THIN FILMS [J].
DHEURLE, FM .
METALLURGICAL TRANSACTIONS, 1971, 2 (03) :683-&
[9]  
DOAN NV, 1975, THIN SOLID FILMS, V34, P165
[10]   ELECTROMIGRATON ACTIVATION-ENERGY DEPENDENCE ON ALCU INTERCONNECT LINEWIDTH AND MICROSTRUCTURE [J].
DREYER, ML ;
VARKER, CJ .
APPLIED PHYSICS LETTERS, 1992, 60 (15) :1860-1862