Effects of surface treatments and metal work functions on electrical properties at p-GaN/metal interfaces

In order to examine the possibility of preparing a nonreacted (nonalloyed) Ohmic contact to p-GaN, the effects of GaN surface treatments and work functions of the contact metals on the electrical properties between the metal contacts and p-GaN were investigated. A contamination layer consisting of GaOx and adsorbed carbons was found on the GaN substrate grown by metalorganic chemical vapor deposition. The contamination layer was not completely removed by sputtering the GaN surface with Ar and N ions where the ion densities were similar to 10(-2) mu A/cm(2). Although the contamination layer was partially removed by immersing in a buffered HF solution, little improvement of the electrical properties of the GaN/metal interfaces was obtained. Most of the contamination layer was removed by annealing the Ni and Ta contacts at temperatures close to 500 degrees C. These annealed contacts exhibited slightly enhanced current injection from the contact metal to the GaN. The present surface treatment study indicated that removal of the contamination layer did not significantly reduce the contact resistance. On the other hand, the resistance decreased exponentially with increasing the metal work functions, where Pt, Ni, Pd, Au, Cu, Ti, Al, Ta, and Ni/Au were deposited on the GaN. This result suggests that the Schottky barrier height at the p-GaN/metal interface might not be pinned at the GaN surface. The present study concluded that a contact metal with a large work function is desirable for nonreacted Ohmic contacts to p-GaN. However, these contacts did not provide the low contact resistance required for blue laser diodes. (C) 1997 American Institute of Physics.