A comparative study of reactive direct current magnetron sputtered CrAlN and CrN coatings

被引:329
作者
Barshilia, Harish C. [1 ]
Selvakumar, N. [1 ]
Deepthi, B. [1 ]
Rajam, K. S. [1 ]
机构
[1] Natl Aerosp Labs, Surface Engn Div, Bangalore 560017, Karnataka, India
关键词
CrN and CrAlN coatings; magnetron sputtering; structure and mechanical properties; thermal stability; surface roughness; corrosion resistance;
D O I
10.1016/j.surfcoat.2006.03.037
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
Approximately 1.5 mu m thick CrN and CrAIN coatings were deposited on silicon and mild steel substrates by reactive direct current (DC) magnetron sputtering. The structural and mechanical properties of the coatings were characterized using X-ray diffraction (XRD) and nanoindentation techniques, respectively. The bonding structure of the coatings was characterized by X-ray photoelectron spectroscopy (XPS). The surface morphology of the coatings was studied using scanning electron microscopy (SEM) and atomic force microscopy (AFM). The XRD data showed that the CrN and CrAIN coatings exhibited B1 NaCl structure. Nanoindentation measurements showed that as-deposited CrN and CrAIN coatings exhibited a hardness of 18 and 33 GPa, respectively. Results of the surface analysis of the as-deposited coatings using SEM and AFM showed a more compact and dense microstructure for CrAIN coatings. The thermal stability of the coatings was studied by heating the coatings in air from 400 to 900 degrees C. The structural changes as a result of heating were studied using micro-Raman spectroscopy. The Raman data revealed that CrN coatings got oxidized at 600 degrees C, whereas in the case of CrAIN coatings, no detectable oxides were formed even at 800 degrees C. After annealing up to 700 degrees C, the CrN coatings displayed a hardness of only about 7.5 GPa as compared to CrAIN coatings, which exhibited hardness as high as 22.5 GPa. The potentiodynamic polarization measurements in 3.5% NaCl solution indicated that the CrAIN coatings exhibited superior corrosion resistance as compared to CrN coatings. (c) 2006 Elsevier B.V. All rights reserved.
引用
收藏
页码:2193 / 2201
页数:9
相关论文
共 42 条
[21]   Improvement of the corrosion resistance of PVD hard coating-substrate systems [J].
Jehn, HA .
SURFACE & COATINGS TECHNOLOGY, 2000, 125 (1-3) :212-217
[22]   Oxidation resistance of Cr1-xAlxN and Ti1-xAlxN films [J].
Kawate, M ;
Hashimoto, AK ;
Suzuki, T .
SURFACE & COATINGS TECHNOLOGY, 2003, 165 (02) :163-167
[23]   Anisotropic lattice expansion and shrinkage of hexagonal TiAlN and CrAlN films [J].
Kimura, A ;
Kawate, M ;
Hasegawa, H ;
Suzuki, T .
SURFACE & COATINGS TECHNOLOGY, 2003, 169 :367-370
[24]  
Kubinski JA, 1999, PLAT SURF FINISH, V86, P20
[25]   XPS investigations of chromium nitride thin films [J].
Lippitz, A ;
Hübert, T .
SURFACE & COATINGS TECHNOLOGY, 2005, 200 (1-4) :250-253
[26]   Oxidation kinetics of sputtered Cr-N hard coatings [J].
Mayrhofer, PH ;
Willmann, H ;
Mitterer, C .
SURFACE & COATINGS TECHNOLOGY, 2001, 146 :222-228
[27]   OXIDATION OF METASTABLE SINGLE-PHASE POLYCRYSTALLINE TI0.5AL0.5N FILMS - KINETICS AND MECHANISMS [J].
MCINTYRE, D ;
GREENE, JE ;
HAKANSSON, G ;
SUNDGREN, JE ;
MUNZ, WD .
JOURNAL OF APPLIED PHYSICS, 1990, 67 (03) :1542-1553
[28]   Thin film of aluminum oxide through pulsed laser deposition: a micro-Raman study [J].
Misra, A ;
Bist, HD ;
Navati, MS ;
Thareja, RK ;
Narayan, J .
MATERIALS SCIENCE AND ENGINEERING B-SOLID STATE MATERIALS FOR ADVANCED TECHNOLOGY, 2001, 79 (01) :49-54
[29]  
MUNZ WD, 1986, J VAC SCI TECHNOL A, V4, P2717, DOI 10.1116/1.573713
[30]   High temperature oxidation behaviour of (Ti1-xCrx)N coatings [J].
Otani, Y ;
Hofmann, S .
THIN SOLID FILMS, 1996, 287 (1-2) :188-192