WEAR BEHAVIOR IN TIN COATINGS MODIFIED BY AN ELECTROLESS NI INTERLAYER ON MILD-STEEL

被引：18

作者：

DOONG, JC

DUH, JG

TSAI, SY

机构：

[1] Department of Materials Science and Engineering, National Tsing Hua University, Hsinchu

来源：

SURFACE & COATINGS TECHNOLOGY | 1993年 / 58卷 / 03期

关键词：

D O I：

10.1016/0257-8972(93)90001-5

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

An electroless nickel deposit is introduced as an interlayer between a carbon steel substrate and r.f.-magnetron-sputtered TiN films, and a compound coating assembly TiN/Ni3P/Fe is derived after appropriate heat treatment. The pin-on-disc test is employed to evaluate the wear behaviour of the fabricated compound coating. The depth profiles of the wear track are measured with an alpha-step and the morphology of the wear track is investigated with the aid of a scanning electron microscope. It is observed that the track depth in TiN/Ni3P/Fe is about an order of magnitude smaller than that in the Fe substrate, and the employment of an electroless Ni interlayer in TiN coating provides beneficial anti-wear resistance.

引用

页码：151 / 155

页数：5

共 7 条

[1] DEPOSITION OF TITANIUM NITRIDE ON SURFACE-HARDENED STRUCTURAL-STEEL BY REACTIVE MAGNETRON SPUTTERING [J].

ALJAROUDI, MY ;

HENTZELL, HTG ;

HORNSTROM, SE ;

BENGTSON, A .

THIN SOLID FILMS, 1989, 182 :153-166

[2] TIN COATINGS ON MILD-STEEL SUBSTRATES WITH ELECTROLESS NICKEL AS AN INTERLAYER [J].

CHEN, YI ;

DUH, JG .

SURFACE & COATINGS TECHNOLOGY, 1991, 48 (02) :163-168

[3] DEPOSITION OF TIN FILMS WITH TITANIUM INTERLAYER ON LOW-CARBON STEEL BY REACTIVE RF MAGNETRON SPUTTERING [J].

CHEN, YI ;

DUH, JG .

SURFACE & COATINGS TECHNOLOGY, 1991, 46 (03) :371-384

[4] A SALT SPRAY TEST ON INTERLAYER-MODIFIED TIN COATING [J].

CHEN, YI ;

DUH, JG ;

CHIOU, BS ;

YANG, TJ .

JOURNAL OF MATERIALS SCIENCE LETTERS, 1992, 11 (12) :810-812

[5] CHEMICALLY VAPOUR-DEPOSITED HARD COATINGS - APPLICATIONS AND SELECTION GUIDELINES [J].

LUX, B ;

HAUBNER, R ;

WOHLRAB, C .

SURFACE & COATINGS TECHNOLOGY, 1989, 38 (03) :267-280

[6] THE EFFECT OF N2 PARTIAL-PRESSURE, DEPOSITION RATE AND SUBSTRATE BIAS POTENTIAL ON THE HARDNESS AND TEXTURE OF REACTIVELY SPUTTERED TIN COATINGS [J].

SPROUL, WD ;

RUDNIK, PJ ;

GRAHAM, ME .

SURFACE & COATINGS TECHNOLOGY, 1989, 39 (1-3) :355-363

[7] A REVIEW OF THE PRESENT STATE OF ART IN HARD COATINGS GROWN FROM THE VAPOR-PHASE [J].

SUNDGREN, JE ;

HENTZELL, HTG .

JOURNAL OF VACUUM SCIENCE & TECHNOLOGY A-VACUUM SURFACES AND FILMS, 1986, 4 (05) :2259-2279

← 1 →