Comparison between a Novel Nickel-Titanium Alloy and 508 Nitinol on the Cyclic Fatigue Life of ProFile 25/.04 Rotary Instruments

被引：140

作者：

Johnson, Eugenia ^{[1
]}

Lloyd, Adain ^{[1
]}

Kuttler, Sergio ^{[1
]}

Namerow, Kenneth ^{[1
]}

机构：

[1] Nova SE Univ, Coll Dent Med, Hlth Profess Div, Dept Endodont, Ft Lauderdale, FL 33328 USA

来源：

JOURNAL OF ENDODONTICS | 2008年 / 34卷 / 11期

关键词：

Canal preparation; cyclic fatigue; M-Wire NiTi; nickel titanium; rotary endodontics;

D O I：

10.1016/j.joen.2008.07.029

中图分类号：

R78 [口腔科学];

学科分类号：

1003 ;

摘要：

ProFile(R) 25/.04 instruments manufactured from three variants of Nitinol (1A, 1B & 2AS) were compared with stock production ProFile 25/.04 instruments and fatigue tested to failure. Cyclic fatigue testing was performed by rotating instruments at 300 RPM in a simulated steel root canal with 5 mm radius and 90 degrees curve until instrument separation. Time to failure was recorded. Torsion testing was undertaken by clamping 3 mm of each instrument tip between brass plates and rotating it at 2 RPM until failure. Data were recorded for torque and angle at fracture. Statistical differences were found with nickel-titanium variant 1B (M-Wire(TM) NiTi) nearly 400% more resistant to cyclic fatigue than stock ProFile 25/.04 (P<.001). Torsion testing found differences between all 508 Nitinol groups and M-Wire(TM) NiTi (P<.001). ProFile 25/.04 files manufactured from M-Wire(TM) NiTi have significantly greater resistance to cyclic fatigue while maintaining comparable torsional properties. (J Endod 2008;34:1406-1409)

引用

页码：1406 / 1409

页数：4

共 31 条

[1] SEM observations of nickel-titanium rotary endodontic instruments that fractured during clinical use [J].

Alapati, SB ;

Brantley, WA ;

Svec, TA ;

Powers, JM ;

Nusstein, JM ;

Daehn, GS .

JOURNAL OF ENDODONTICS, 2005, 31 (01) :40-43

[2] Proposed role of embedded dentin chips for the clinical failure of nickel-titanium rotary instruments [J].

Alapati, SB ;

Brantley, WA ;

Svec, TA ;

Powers, JM ;

Nusstein, JM ;

Daehn, GS .

JOURNAL OF ENDODONTICS, 2004, 30 (05) :339-341

[3] Influence of simulated clinical use on the torsional behavior of nickel-titanium rotary endodontic instruments [J].

Bahia, MGA ;

Melo, MCC ;

Buono, VTL .

ORAL SURGERY ORAL MEDICINE ORAL PATHOLOGY ORAL RADIOLOGY AND ENDODONTOLOGY, 2006, 101 (05) :675-680

[4] Physical and mechanical characterization and the influence of cyclic loading on the behaviour of nickel-titanium wires employed in the manufacture of rotary endodontic instruments [J].

Bahia, MGA ;

Martins, RC ;

Gonzalez, BM ;

Buono, VTL .

INTERNATIONAL ENDODONTIC JOURNAL, 2005, 38 (11) :795-801

[5]

Berendt CJ, 2006, INT C SHAP MEM SUP T

[6] Torsional fatigue and endurance limit of a size 30.06 ProFile rotary instrument [J].

Best, S ;

Watson, P ;

Pilliar, R ;

Kulkarni, GGK ;

Yared, G .

INTERNATIONAL ENDODONTIC JOURNAL, 2004, 37 (06) :370-373

[7] Effect of electropolishing ProFile nickel-titanium rotary instruments on cyclic fatigue resistance, torsional resistance, and cutting efficiency [J].

Bui, Tung B. ;

Mitchell, John C. ;

Baumgartner, J. Craig .

JOURNAL OF ENDODONTICS, 2008, 34 (02) :190-193

[8] Comparison of defects in ProTaper hand-operated and engine-driven instruments after clinical use [J].

Cheung, G. S. P. ;

Bian, Z. ;

Shen, Y. ;

Peng, B. ;

Darvell, B. W. .

INTERNATIONAL ENDODONTIC JOURNAL, 2007, 40 (03) :169-178

[9] Defects in ProTaper S1 instruments after clinical use: fractographic examination [J].

Cheung, GSP ;

Peng, B ;

Bian, Z ;

Shen, Y ;

Darvell, BW .

INTERNATIONAL ENDODONTIC JOURNAL, 2005, 38 (11) :802-809

[10] POTENTIAL APPLICATIONS OF CERTAIN NICKEL-TITANIUM (NITINOL) ALLOYS [J].

CIVJAN, S ;

HUGET, EF ;

DESIMON, LB .

JOURNAL OF DENTAL RESEARCH, 1975, 54 (01) :89-96

← 1 2 3 4 →