Large-grained polycrystalline Si films obtained by selective nucleation and solid phase epitaxy

被引:13
作者
Puglisi, RA [1 ]
Tanabe, H [1 ]
Chen, CM [1 ]
Atwater, HA [1 ]
机构
[1] CALTECH, Thomas J Watson Lab Appl Phys, Pasadena, CA 91125 USA
来源
MATERIALS SCIENCE AND ENGINEERING B-SOLID STATE MATERIALS FOR ADVANCED TECHNOLOGY | 2000年 / 73卷 / 1-3期
关键词
solar cells; Si; selective nucleation; Ni; In;
D O I
10.1016/S0921-5107(99)00466-3
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
We investigated the formation of large-grain polycrystalline silicon films on glass substrates for application in low-cost thin film crystalline silicon solar cells. Since the use of glass substrates constrains process temperatures, our chosen approach to form large-grain polycrystalline silicon templates is selective nucleation and solid phase epitaxy (SNSPE). In this process. selective crystallization of an initially amorphous silicon film, at lithographically predetermined sites, enables grain sizes larger than those observed via random crystallization. Selective heterogeneous nucleation centers were created for both P-doped, B-doped and undoped. 100 nm thick amorphous silicon films. by masked implantation of In or Ni islands, followed by annealing at temperatures below 600 degrees C. Seeded crystallization begins at the metal islands and continues via lateral solid phase epitaxy (SPE), thus obtaining crystallized regions of several tens of square microns. The maximum achievable grain size depends on the product of the SPE rate and the incubation time for the spontaneous nucleation. We have studied the dependence of the SPE rate and the incubation time on the type of metal (In and Ni) inducing the nucleation and on the electronic dopant (e.g. P and B) concentration in the 10(19)-10(21) cm(-3) range. (C) 2000 Elsevier Science S.A. All rights reserved.
引用
收藏
页码:212 / 217
页数:6
相关论文
共 11 条
[1]   Polycrystalline Si films fabricated by low temperature selective nucleation and solid phase epitaxy process [J].
Chen, CM ;
Atwater, HA .
THIN-FILM STRUCTURES FOR PHOTOVOLTAICS, 1998, 485 :67-72
[2]  
GRAFF K, SPRINGER SERIES MAT, V24
[3]   SILICIDE FORMATION AND SILICIDE-MEDIATED CRYSTALLIZATION OF NICKEL-IMPLANTED AMORPHOUS-SILICON THIN-FILMS [J].
HAYZELDEN, C ;
BATSTONE, JL .
JOURNAL OF APPLIED PHYSICS, 1993, 73 (12) :8279-8289
[4]   RECRYSTALLIZATION OF AMORPHIZED POLYCRYSTALLINE SILICON FILMS ON SIO2 - TEMPERATURE-DEPENDENCE OF THE CRYSTALLIZATION PARAMETERS [J].
IVERSON, RB ;
REIF, R .
JOURNAL OF APPLIED PHYSICS, 1987, 62 (05) :1675-1681
[5]   NICKEL ATOMIC DIFFUSION IN AMORPHOUS-SILICON [J].
KUZNETSOV, AY ;
SVENSSON, BG .
APPLIED PHYSICS LETTERS, 1995, 66 (17) :2229-2231
[6]   IMPURITY-STIMULATED CRYSTALLIZATION AND DIFFUSION IN AMORPHOUS-SILICON [J].
NYGREN, E ;
POGANY, AP ;
SHORT, KT ;
WILLIAMS, JS ;
ELLIMAN, RG ;
POATE, JM .
APPLIED PHYSICS LETTERS, 1988, 52 (06) :439-441
[7]  
SPAEPEN F, 1992, NATO ADV SCI INST SE, V222, P483
[8]   SECONDARY GRAIN-GROWTH IN THIN-FILMS OF SEMICONDUCTORS - THEORETICAL ASPECTS [J].
THOMPSON, CV .
JOURNAL OF APPLIED PHYSICS, 1985, 58 (02) :763-772
[9]   TRANSITION-METALS IN SILICON [J].
WEBER, ER .
APPLIED PHYSICS A-MATERIALS SCIENCE & PROCESSING, 1983, 30 (01) :1-22
[10]  
YAMAGUCHI M, J APPL PHYS, V60, P413