EFFECT OF OXYGEN ON THE FORMATION OF END-OF-RANGE DISORDER IN IMPLANTATION AMORPHIZED SILICON

被引:7
作者
LORENZ, E
GYULAI, J
FREY, L
RYSSEL, H
KHANH, NQ
机构
[1] TECH UNIV BUDAPEST,JOINT INST EXPTL PHYS,H-1525 BUDAPEST,HUNGARY
[2] HUNGARIAN ACAD SCI,CENT RES INST PHYS,H-1525 BUDAPEST,HUNGARY
关键词
D O I
10.1557/JMR.1991.1695
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Formation of End-of-Range (EOR) disorder was studied in (100)-oriented silicon, when subjected to amorphization by implantation of Ge+ ions, followed by a 10 s Rapid Thermal Annealing (RTA) at 1050-degrees-C. XTEM, RBS/channeling, and SIMS were used to analyze Czochralski grown (CZ) silicon wafers with oxygen concentrations of 6.5, 7.0, and 8.0 x 10(17) / cm3 and Float Zone (FZ) silicon, as "low oxygen" wafers. Amorphization on neighboring parts of the 4" wafers was made either by 60 keV Ge+ implantation or by 110 keV Ge+ implantation and by sequential (60 keV + 110 keV) Ge+ implantation. Parts of each wafer were additionally implanted with 13 keV boron. In FZ silicon, no defects were found for 60 keV Ge+ implantation and RTA at 1050-degrees-C. For 110 keV Ge+ and sequential (60 keV + 110 keV) Ge+ implantation in FZ-silicon the majority of the samples showed perfect annealing. Two wafers, however, subjected to sequential implantation still contained defects but with a defect density that was one order of magnitude lower than for CZ wafers. For one of them, not even a continuous layer of defects was formed. In contrast, CZ wafers contained defect bands, except for the 60 keV Ge+ implantation [in accord with the findings of Ozturk et al., IEEE Trans. on Electronic Dev. 35, 659 (1988)]. The presence of boron had no visible effect on the defect structure.
引用
收藏
页码:1695 / 1700
页数:6
相关论文
共 14 条
[1]   ELIMINATION OF END-OF-RANGE AND MASK EDGE LATERAL DAMAGE IN GE+ PREAMORPHIZED, B+ IMPLANTED SI [J].
AJMERA, AC ;
ROZGONYI, GA .
APPLIED PHYSICS LETTERS, 1986, 49 (19) :1269-1271
[2]   REORDERING OF AMORPHOUS LAYERS OF SI IMPLANTED WITH P-31, AS-75, AND B-11 IONS [J].
CSEPREGI, L ;
KENNEDY, EF ;
GALLAGHER, TJ ;
MAYER, JW ;
SIGMON, TW .
JOURNAL OF APPLIED PHYSICS, 1977, 48 (10) :4234-4240
[3]   THE ROLE OF TRANSIENT DAMAGE ANNEALING IN SHALLOW JUNCTION FORMATION [J].
FAIR, RB .
NUCLEAR INSTRUMENTS & METHODS IN PHYSICS RESEARCH SECTION B-BEAM INTERACTIONS WITH MATERIALS AND ATOMS, 1989, 37-8 :371-378
[4]  
FAIR RB, 1990, SOLID STATE TECHNOL, P107
[5]  
GANIN E, 1987, MATER RES SOC S P, V74, P717
[6]   SUB-100-NM P+-N SHALLOW JUNCTIONS FABRICATED BY GROUP-III DUAL ION-IMPLANTATION AND RAPID THERMAL ANNEALING [J].
LIN, CM ;
STECKL, AJ ;
CHOW, TP .
APPLIED PHYSICS LETTERS, 1989, 54 (18) :1790-1792
[7]  
MAHER DM, 1986, MATER RES SOC S P, V52, P93
[8]  
MULLER H, 1971, ION IMPLANTATION SEM, P85
[9]   ELECTRICAL-PROPERTIES OF IMPLANTED AND RAPID THERMAL ANNEALED SHALLOW P+-N JUNCTIONS [J].
OZGUZ, VH ;
WORTMAN, JJ ;
HAUSER, JR ;
SIMPSON, L ;
LITTLEJOHN, MA ;
CHU, WK ;
ROZGONYI, GA .
APPLIED PHYSICS LETTERS, 1984, 45 (11) :1225-1226
[10]   OPTIMIZATION OF THE GERMANIUM PREAMORPHIZATION CONDITIONS FOR SHALLOW-JUNCTION FORMATION [J].
OZTURK, MC ;
WORTMAN, JJ ;
OSBURN, CM ;
AJMERA, A ;
ROZGONYI, GA ;
FREY, E ;
CHU, WK ;
LEE, C .
IEEE TRANSACTIONS ON ELECTRON DEVICES, 1988, 35 (05) :659-668