SUPPRESSION MECHANISMS FOR OXIDATION STACKING-FAULTS IN SILICON ON INSULATOR

被引:17
作者
GUILLEMOT, N
TSOUKALAS, D
TSAMIS, C
MARGAIL, J
PAPON, AM
STOEMENOS, J
机构
[1] NCSR DEMOCRITOS,INST MICROELECTR,GR-15310 ATHENS,GREECE
[2] CEN,CEA,ELECTR & TECHNOL INFORMAT LAB,F-38041 GRENOBLE,FRANCE
[3] UNIV THESSALONIKI,DEPT PHYS,GR-54006 SALONIKA,GREECE
关键词
D O I
10.1063/1.351202
中图分类号
O59 [应用物理学];
学科分类号
摘要
Oxidation of the Si overlayer in silicon separated by oxygen (SIMOX) is expected to form oxidation stacking faults (OSF) since this process generates Si interstitials into the active Si layer. In spite of this process, recent experiments reveal that the density of OSF is very low. A possible mechanism to explain the absence of OSF in SIMOX is that Si interstitials rejected from the Si-overlayer/SiO2 interface could react with the SiO2 of the buried layer to form SiO molecules (Si + SiO2 = 2SiO). These species, which can diffuse four orders of magnitude faster than Si through the SiO2 buried layer, are recombined by the reverse reaction at the back interface due to the absence of Si-interstitial supersaturation. Since the activation energy for this process is 4.4 eV, OSF can be generated if the Si overlayer is subjected to a preoxidation treatment that introduces a high density of stacking fault (SF) nucleation sites, because of the activation energy for heterogeneous generation of OSF is only 2.3 eV. In this case 0.21 x 10(-3) of Si interstitials are incorporated in OSF over the total Si atoms that are consumed during the oxidation. This value agrees with the proportion of Si interstitials incorporated in OSF when the SiO2 buried layer is replaced by a Si3N4 buried layer since this layer is a barrier for the Si-interstitial migration to the substrate. The value 0.21 x 10(-3) is very close to the expected theoretical value revealing that almost all the Si interstitials were captured by the OSF.
引用
收藏
页码:1713 / 1720
页数:8
相关论文
共 32 条
[1]   FILM STRESS-RELATED VACANCY SUPERSATURATION IN SILICON UNDER LOW-PRESSURE CHEMICAL VAPOR-DEPOSITED SILICON-NITRIDE FILMS [J].
AHN, ST ;
KENNEL, HW ;
PLUMMER, JD ;
TILLER, WA .
JOURNAL OF APPLIED PHYSICS, 1988, 64 (10) :4914-4919
[2]  
Amelinckx S., 1964, DIRECT OBSERVATION D
[3]  
BALLUFFI RW, 1979, DISLOCATIONS SOLIDS, V4, P95
[4]   BARRIER TO MIGRATION OF THE SILICON SELF-INTERSTITIAL [J].
BARYAM, Y ;
JOANNOPOULOS, JD .
PHYSICAL REVIEW LETTERS, 1984, 52 (13) :1129-1132
[5]   DIFFUSION OF SILICON IN AMORPHOUS SILICA [J].
BREBEC, G ;
SEGUIN, R ;
SELLA, C ;
BEVENOT, J ;
MARTIN, JC .
ACTA METALLURGICA, 1980, 28 (03) :327-333
[6]  
BRONNER GB, 1985, MATER RES SOC S P, V36, P49
[7]   MICROSCOPIC THEORY OF IMPURITY-DEFECT REACTIONS AND IMPURITY DIFFUSION IN SILICON [J].
CAR, R ;
KELLY, PJ ;
OSHIYAMA, A ;
PANTELIDES, ST .
PHYSICAL REVIEW LETTERS, 1985, 54 (04) :360-363
[8]   MICROSCOPIC THEORY OF ATOMIC DIFFUSION MECHANISMS IN SILICON [J].
CAR, R ;
KELLY, PJ ;
OSHIYAMA, A ;
PANTELIDES, ST .
PHYSICAL REVIEW LETTERS, 1984, 52 (20) :1814-1817
[9]   HIGH-TEMPERATURE STABILITY OF SI/SIO2 INTERFACES AND THE INFLUENCE OF SIO FLUX ON THERMOMIGRATION OF IMPURITIES IN SIO2 [J].
CELLER, GK ;
TRIMBLE, LE .
APPLIED PHYSICS LETTERS, 1988, 53 (25) :2492-2494
[10]   CATALYTIC EFFECT OF SIO ON THERMOMIGRATION OF IMPURITIES IN SIO2 [J].
CELLER, GK ;
TRIMBLE, LE .
APPLIED PHYSICS LETTERS, 1989, 54 (15) :1427-1429